Improved type casting material based on bauxite for middle-small type ladle and preparation method

An improved technology of ladle casting, which is applied in the field of refractory materials, can solve problems such as spalling, shrinkage and easy cracks, and achieve the effect of improving compressive strength and flexural strength

Inactive Publication Date: 2007-01-24
上海彭浦特种耐火材料厂有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, only magnesia fine powder is added to the aluminum-magnesium castable. Under the action of high temperature, the reaction of aluminum-magnesium

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0037] Example 1

[0038] Ladle castable content Al 2 O 3 The mass percentage is 70.5, and MgO is 10.8. The specific proportion is 20-10mm bauxite 15%, 10-5mm bauxite 10%, 5-3mm bauxite 8%, 3-1mm bauxite 10%, 1mm-75μm bauxite 15%, ≤75μm bauxite 11.5% ; 4-2mm sintered magnesia 2%, 2-1mm sintered magnesia 2%, 1mm-75μm fused magnesia 2%, ≤75μm fused magnesia 4.8%, brown corundum powder 2.6%, silica powder 2.4% , Sodium tripolyphosphate 0.5%. Weigh according to the above ratio, and then premix the three additives with the components ≤1mm, then mix them with other particles, and set aside.

Example Embodiment

[0039] Example 2

[0040] Provide ladle castable Al 2 O 3 The mass percentage is 74.8, MgO13.60. The particle grading ratio is 20-10mm bauxite 10%, 10-5mm bauxite 12%, 5-3mm bauxite 18%, 3-1mm bauxite 15%, 1mm-75μm bauxite 5%, ≤75μm bauxite 10%; 4-2mm sintered magnesia 3%, 2-1mm sintered magnesia 4%, 1mm-75μm fused magnesia 3%, ≤75μm fused magnesia 5%, ≤5μm brown corundum powder 2.2%, two Silica powder (≤5μm) 2%, sodium tripolyphosphate 0.2%. After weighing according to the formula, the three additives are premixed with the components ≤1mm and then mixed with other particles, and set aside.

[0041] Item

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention provides an improved type alumina base medium and small ladle pouring material and its preparation method. It is characterized by that it is prepared by using electrofused magnesium sand and sintered magnesium sand through the process of continuous granule-grade preparation, in is matrix a brown corundum micropowder is added, so that the aluminium-magnesium spinel phase is produced at high temperature, and the ratio of silicon dioxide micropowder and magnesium sand fine powder can be reasonably controlled so as to make the alumina base have good low-temperature, medium temperature and high-temperature strength.

Description

technical field [0001] The invention relates to an improved bauxite-based ladle castable with improved components and its preparation method, in particular to a long-life bauxite-based small and medium-sized ladle castable prepared by continuous particle gradation of fused magnesia and sintered magnesia and Preparation method. It belongs to the field of refractory materials. Background technique [0002] Alumina-based aluminum-magnesium castables have excellent performance, and have achieved good results when used in small and medium-sized ladles. The technical route of this type of material is to add MgO powder to the matrix of high-alumina materials so that they can be used at high temperatures. Form aluminum-magnesium spinel, spinel has a small thermal expansion coefficient and elastic modulus, the melting point is 2135 ° C, and produces volume expansion effect when formed, so that the material has high refractoriness and good slag resistance , Thermal shock stability. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/66C04B35/10C04B35/04C04B35/20
Inventor 何晓俊
Owner 上海彭浦特种耐火材料厂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap