Steel, molten iron slag gathering heat insulating covering agent possessing sulfur phosphorus eliminating function

A technology of thermal insulation covering agent and function, which is applied in the fields of hot metal slag accumulation, steel, and thermal insulation covering agent. It can solve the problems of weak slag accumulation ability, poor thermal insulation performance, and molten steel pollution, and achieves good falling performance and good covering performance. , the effect of preventing light and heat radiation

Inactive Publication Date: 2007-04-25
高申明
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The covering agent is widely used in the metallurgical casting industry such as various gray cast iron, ductile iron and various cast steel liquid production processes. The use of this covering agent is an effective measure to eliminate casting pores, slag inclusions, and prevent nodular iron spheroidization decline. Traditional covering agents use grass ash, perlite, quartz stone, etc. These covering agents are added in a large amount during use, the slag accumulation ability is not strong, the thermal insulation performance is poor, and there is certain pollution to molten steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1   Embodiment 2

[0008] Embodiment one Embodiment two Embodiment three Embodiment Embodiment five

[0009] m 2 S sand powder 100 150 180 250 280

[0010] Slag 200 220 230 240 260

[0011] Power plant ash 100 180 200 260 280

[0012] Zeolite 50 60 70 75 100

[0013] Graphite 30 50 60 80 100

[0014] Water 14.4 33 37 72.4 102

[0015] Guilin No. 1 Powder 60 65 70 75 80

[0016] Perlite 200 220 270 260 300

[0017] The preparation method of the present invention is: M 2 S Sand powder, slag, power plant ash, zeolite and graphite are mixed according to the above ratio, then add water and stir for 1-5 minutes, then add perlite and Guilin No. 1 powder and mix for 5-10 minutes; Sieve granulation, collect granules with a concentration of 80% and put them into the oven for drum drying. After the material is cooled, the product is obtained.

[0018] m 2 S is Mg 2 SiO 4 , is the abbreviated chemical structure formula of forsterite. m 2 S sand powder is made from M 2 S is obtained b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A slag-gathering and insulating covering agent able to remove S and P from molten steel or iron is prepared from M2S sand, slag, pearlite powdered coal ash, zeolite, graphite and the powder 'Guilin No.one'. Its advantages are high effect to remove S and P and shield light, low temp drop, and no pollution to molten steel or iron.

Description

technical field [0001] The invention relates to a covering agent for accumulating slag and heat preservation of steel and molten iron, in particular to a covering agent for accumulating slag and heat preservation of steel and molten iron with the function of removing sulfur and phosphorus. Background technique [0002] The covering agent is widely used in the metallurgical casting industry such as various gray cast iron, ductile iron and various cast steel liquid production processes. The use of this covering agent is an effective measure to eliminate casting pores, slag inclusions, and prevent nodular iron spheroidization decline. Traditional covering agents use grass ash, perlite, quartz stone, etc. These covering agents are added in a large amount during use, have weak slag accumulation ability, poor thermal insulation performance, and have certain pollution to molten steel. Contents of the invention [0003] The object of the present invention is to provide a steel and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D1/00
Inventor 高申明汪光银高俊
Owner 高申明