Finishing process for nano three-protective dacron fabrics

A polyester fabric, nanotechnology, applied in fiber processing, textiles and papermaking, etc., can solve the problems of unsatisfactory anti-fouling effect, poor durability and washability, large dosage, etc., to increase the three-proof effect and maintain warmth. and fluffy, low production cost effect

Inactive Publication Date: 2003-06-18
HEBEI UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF1 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with traditional water-repellent agents, it has better water-repellent, oil-repellent, and anti-fouling properties, but the dosage is large, and the anti-fouling effect is not very ideal. The problem of poor washability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] ①Polyester fabric to be finished: pure polyester plain weave fabric, its specification is 75D×75D×180×1500.

[0025] ② Preparation of finishing solution: In the preparation, the dosage of organic fluorine three-proofing agent is 100 g / liter, and AG710 is selected. The dosage of the composite nanomaterial dispersion is 0.5 g / liter, and the dispersion system containing nano-zinc oxide and titanium oxide is selected, and the solid content is 25%; the dosage of the soft self-crosslinking adhesive is 6 grams / liter, and the rest is water. Soft water can be used for water. When preparing the finishing liquid, it is best to add water, organic fluorine finishing agent, composite nanomaterial dispersion, and soft self-crosslinking adhesive to the high-level tank for mixing, and stir continuously for 30 minutes, then put into the rolling groove.

[0026] ③ Finish the polyester fabric by padding method: use a uniform pad car, two dipping and two rolling, the dipping temperature of ...

Embodiment 2

[0031] ①Polyester fabric to be finished: pure polyester plain weave fabric, its specification is 75D×75D×230×1500.

[0032] ② Preparation of finishing solution: In the preparation, the dosage of organic fluorine three-proofing agent is 50 g / liter, and AG418 is selected. The dosage of the composite nanomaterial dispersion liquid is 1.5 grams per liter, and the dispersion system containing nano-zinc oxide and titanium oxide is selected for use, and the solid content is 15%; the dosage of the soft self-crosslinking adhesive is 20 grams per liter, and the rest is water. Soft water can be used for water. When preparing the finishing liquid, it is best to add water, organic fluorine finishing agent, composite nanomaterial dispersion, and soft self-crosslinking adhesive to the high-level tank for mixing, and stir continuously for 30 minutes, then put into the rolling groove.

[0033] ③ Finish the polyester fabric by padding method: use a uniform padding car, one dipping and one rol...

Embodiment 3

[0038] ①Polyester fabric to be finished: pure polyester plain weave fabric, its specification is 75D×75D×210×1500.

[0039] ② Preparation of finishing solution: In the preparation, the dosage of organic fluorine three-proofing agent is 50 g / L, and AG710 is selected. The dosage of the composite nanomaterial dispersion is 1.0 g / liter, and the dispersion system containing nano-zinc oxide and titanium oxide is selected for use, and the solid content is 15%; the dosage of the soft self-crosslinking adhesive is 12 grams / liter, and the rest is water. Soft water can be used for water. When preparing the finishing liquid, it is best to add water, organic fluorine finishing agent, composite nanomaterial dispersion, and soft self-crosslinking adhesive to the high-level tank for mixing, and stir continuously for 30 minutes, then put into the rolling groove.

[0040] ③ Finish the polyester fabric by padding method: use a uniform pad car, two dipping and two rolling, the dipping temperatu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

A technology for finishing the water-, oil-and dirt repellent polyester fabric includes such steps as preparing the finishing liquid from organofluorine composite nano material dispersed liquid and flexible-type self-crosslinking adhesive, dipping it in the finishing liquid for 0.5-1 min, squeezing, prebaking at 100-110 deg.C for 1-2 min, and baking at 130-180 deg.C for 3-5 min. Its advantages are excellent "three repelling" function, better durability and high washing resistance.

Description

technical field [0001] The invention relates to a water-repellent, oil-repellent and antifouling finishing method for polyester fabrics. Background technique [0002] At present, the following finishing agents are mainly used for fabric waterproofing at home and abroad: paraffin-aluminum soaps, pyridinium quaternary ammonium salts, methylol melamine derivatives, chromium stearate complexes, organic silicon, etc., and their common feature is that they do not reject Oily, not stain-resistant, poor washability. In recent years, fluorine-containing compounds have been gradually used in fabric water repellency, oil repellency and antifouling finishing. Compared with traditional water-repellent agents, it has better water-repellent, oil-repellent, and anti-fouling properties, but the dosage is large, and the anti-fouling effect is not very ideal, and there are durability and The problem of poor washability. Nanotechnology is a new high-tech emerging in t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/08
Inventor 张永久冯爱芬魏玉娟戚军芳朱俊萍
Owner HEBEI UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com