Spray casting-suction casting method and equipment for preparing large non crystal alloy

A technology of amorphous alloys and large blocks, which is applied in the field of vacuum spray casting-suction casting preparation of large amorphous alloys, which can solve the problems of complex copper mold manufacturing and achieve the effect of high-speed filling and dense forming

Inactive Publication Date: 2003-09-17
UNIV OF SCI & TECH BEIJING
View PDF1 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After the master alloy is melted, the baffle between the upper and lower copper molds is opened, and the liquid alloy is sucked into the water-cooled copper mold below under the action of vacuum suction, and the bulk amorphous is prepared by the strong cooling effect of the water-cooled copper mold. The disadvantage of this equipment is Copper mold manufacturing is complex, considering not only the shape of the sample, but also the vacuum sealing of the copper mold

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spray casting-suction casting method and equipment for preparing large non crystal alloy
  • Spray casting-suction casting method and equipment for preparing large non crystal alloy
  • Spray casting-suction casting method and equipment for preparing large non crystal alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] Five high-purity pure metals are selected, namely Zr (99.99wt%), Ti (99.995wt%), Cu (99.95wt%), Ni (99.95wt%), Be (99.999wt%). The atomic percentage is: Zr is 40, Cu is 10, Ni is 11, Ti is 5, and Be is 25. Under the protection of argon gas with a purity of 99.8%, the purification technology of liquid master alloy is applied and arc melting is used. The master alloy is prepared by the method. In order to ensure the homogeneity of each component in the master alloy, the master alloy was remelted three times. The surface of the master alloy ingot is mechanically ground and polished to remove surface oxide scale, then crushed into small pieces and the surface is cleaned with alcohol. These master alloy fragments are broken into graphite crucibles, utilize the device as shown in accompanying drawing 1, according to the working principle as mentioned above, prepare Zr as shown in accompanying drawing 2 40 Ti 14 Ni 11 Cu 10 be 25bar. Using an X-ray diffractometer, the d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A spray casting-suction casing apparatus for preparing great non-crystal alloy block is composed of upper and lower furnace chambers, water-cooled partition between said chambers, heating body consisting of one Mo sheet layer and 6 reflecting screen layers, mould made of quartz glass or graphite arranged in said heating body and passing through said partition, U-shaped seals, plug pulling unit for the quartz glass (or graphit) plug of the circular hole on the bottom of mould, and water-cooled copper mould made of red copper.

Description

Technical field: [0001] The invention belongs to the technical field of spray-casting-suction casting of bulk amorphous alloys, and in particular provides a preparation method of vacuum spray-casting-suction casting of bulk amorphous alloys and corresponding equipment. Background technique: [0002] Bulk amorphous alloy materials are a class of advanced materials developed rapidly in the 1990s. Compared with traditional crystalline alloy materials, bulk amorphous alloys have more excellent mechanical properties, the ability to resist corrosion by various media, good soft and hard magnetic properties, and unique expansion characteristics. Bulk amorphous alloys have very attractive application prospects. In the early nineties, A.Inoue, T Zhang and T.Masumoto.Mater.Trans., JIM, 30(1989), 965 and American A.Peker and W.L.Johnson, Appl.Phys.Lett., 63(1993), 2342 breaks through the high-speed cooling (>10 6 K / s) limit, so that under the cooling rate condition that convention...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B22D18/06C22C45/10
Inventor 惠希东寇宏超陈俊崔新发陈国良
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More