Anti-oxidation silica carbide pouring material

A silicon carbide and castable technology, applied in the field of refractory materials, can solve the problems of the influence of construction thickness, the service life is not long, and it is difficult to adapt, so as to overcome the loose local structure, increase the usable time, and improve the usable time.

Inactive Publication Date: 2003-10-22
宜兴天霸非金属材料有限公司
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The quality of the refractory material in the furnace is the key to the long-term and full-load safe production of the waste incinerator, especially the lower part of the walls on both sides of the waste incinerator, due to the volatile gas, molten matter, fly ash and slag generated by waste incineration, etc., Refractory materials are also required to have good wear resistance, corrosion resistance, slag resistance, and oxidation resistance. At present, refractory materials used in waste incinerators at home and abroad are usually silicon carbide castables, which use silicon carbide particles as aggregates to pass through It is made of low-cement micro-powder, and there are obvious deficiencies in actual use and construction, which are manifested in: 1. The particle size of silicon carbide particles used as aggregate is less than or equal to 5 mm, which is brought about by the process of producing silicon carbide with the principle of sintering. As a result, the critical size of the particles is difficult to exceed 5 mm, and there are more pseudo-particles between the 5-3 mm silicon carbide particles. As aggregates, it is easy to cause structural looseness of the castable, and the construction thickness is also affected. Second, the volatilization and incineration temperature of harmful gases in the waste incinerator is between 650-1100°C, which is the weakest oxidation section of the silicon carbide castable, although the castable is added with aluminum oxide to increase its strength And sintering aid silica fume, but it has not fundamentally improved the oxidation resistance of the castable; Third, the castable uses alumina cement as a binder. This single binder makes the usable time of the castable unable to be adjusted arbitrarily. It is difficult to adapt to the specific occasions where the temperature difference between east, west, north and south is large, and the air humidity is greatly different, and the construction quality in various environments cannot be guaranteed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Example 1, the anti-oxidation silicon carbide castable suitable for spring and autumn, its component weight ratio relationship is:

[0029] Large crystalline silicon carbide particles 7-5mm 20 parts

[0030] 5-3mm 15 parts

[0031] 3-1mm 20 parts

[0032] 1-0mm 16 parts

[0033] Silicon carbide matrix <320 mesh 10 parts

[0034] Fast alumina cement 5 parts

[0035] Slow alumina cement 5 parts

[0036] al 2 o 3 Micropowder ≤4μm 5 parts

[0037] SiO 2 Micropowder ≤1μm 4 parts

[0038] Plus:

[0039] 0.15 parts of boric acid

[0040] Aluminum powder 0.3 parts

[0041] 0.8 part of silicon fume Example 2 is applicable to the anti-oxidation silicon carbide castable in winter, and its component weight ratio relationship is:

[0042] Large crystalline silicon carbide particles 7-5mm 18 parts

[0043] 5-3mm 16 parts

[0044] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to an antioxidant silicon arbide pouring material, belonging to the field of refractory material technology. Its composition includes: large crystal silicon carbide granules whose grain size is less than or equal to 7 mm 68-72%, alumina cement 2-12%, silicon carbide matrix whose grain size is less than or equal to 320 meshes 8-10%, alpha-Al2O3 micrpowder whose grain size is less than or equal to 4 micrometers 5-6 %, SiO2 micropowder whose grain size ia less than or equal to 1 micrometer 4-5 % and boric acid 0.1-0.3% and composite antioxidant 1-2%. Said pouring material raises resistance to oxidation, reduces porosity, raises resistance to slag corrosion, can make its service time have adjustability, and can improve furnace adaptability, and can raise the service life of incinerator.

Description

technical field [0001] The invention relates to a refractory material, in particular to an anti-oxidation silicon carbide casting material used in a garbage incinerator. technical background [0002] The quality of the refractory material in the furnace is the key to the long-term and full-load safe production of the waste incinerator, especially the lower part of the walls on both sides of the waste incinerator, due to the volatile gas, molten matter, fly ash and slag generated by waste incineration, etc., Refractory materials are also required to have good wear resistance, corrosion resistance, slag resistance, and oxidation resistance. At present, refractory materials used in waste incinerators at home and abroad are usually silicon carbide castables, which use silicon carbide particles as aggregates to pass through It is made of low-cement micro-powder, and there are obvious deficiencies in actual use and construction, which are manifested in: 1. The particle size of sil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/565C04B35/622C04B35/626C04B35/66
Inventor 吴国强钱军峰
Owner 宜兴天霸非金属材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products