Water soluble thermosetting acrylate cold rolled silicon steel coating

A technology of water-soluble acrylic acid and acrylic resin, which is applied in coatings and devices for coating liquid on the surface, and can solve problems such as harm to the human physiological system

Inactive Publication Date: 2004-02-04
许守煜
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The coating mentioned in Chinese patent 98,125,437 uses commercially available acidic acrylic resin to prepare this type of coating, which mainly improves the water absorption performance of the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Monomer dosage: Water-soluble acrylic resin: 59 parts

[0017] Inorganic solid filler: 22 parts

[0018] Cross-linking agent: 19 parts

[0019] Add inorganic solid filler and cross-linking agent to water-soluble acrylic resin, mix and stir evenly, then add water-soluble acrylic resin, inorganic solid filler and 30% deionized water of the total amount of cross-linking agent, release to viscosity in deionized water For 15 seconds (measured by Tu-4 viscometer, temperature 25°C), and finally put into the bucket to evenly mix the material, and sand mill it.

Embodiment 2

[0021] Inorganic solid filler

[0022] 35 parts of zinc phosphate;

[0023] 27 parts of Gaocen soil

[0024] illite 35 parts

[0025] 3 parts titanium dioxide

[0026] Mix and stir evenly. Cross-linking agent: high-etherified melamine resin monomer dosage Water-soluble acrylic resin: 61 parts Inorganic solid filler: 20 parts Cross-linking agent: 19 parts,

[0027] Add inorganic solid filler and crosslinking agent to water-soluble acrylic resin, mix and stir evenly, then add water-soluble acrylic resin, inorganic solid filler and 40% deionized water of the total amount of crosslinking agent, release to viscosity in deionized water For 25 seconds, (measured by Tu-4 viscometer, temperature 25°C), and finally put into the bucket to evenly mix the material, and make it by sand milling.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A water-soluble thermosetting acrylate paint for cold-rolled silicon steel is prepared from water-soluble acrylic acid, inorganic solid filler and cross-linking agent through proportionally mixing them together, stirring, adding deionized water for deluting it, homogenizing and sand grinding. Its advantages are high resistance to cold and weather, high adhesion, uniform color, and high antirust performance.

Description

technical field [0001] The invention relates to a subnano-level water-soluble thermosetting acrylate cold-rolled silicon steel coating. The invention belongs to the technical field of paint application. Background technique [0002] So far, there are many technologies and coating formulations for forming an insulating layer on conductive steel sheets. The earliest coatings were mainly chromate and phosphate to form an inorganic film on the conductive steel sheet. Although the inorganic film is excellent in heat resistance, it is poor in water resistance, impact resistance, and adhesion. Recently, in order to solve the above problems, there have been some methods using hybrid coating formulations containing two main components, organic and inorganic. This formulation takes full advantage of the good solderability and heat resistance of inorganic films and the excellent water resistance, insulation, impact resistance and adhesion of organic films. For example, in the coati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B05D7/14C09D133/04
Inventor 许守煜徐兴良许敏峰
Owner 许守煜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap