Predispersions, process for their preparation, compositions therefor, process for the preparation of such compositions

A dispersion and mixture technology, applied in the field of pre-dispersion, preparation of the pre-dispersion, composition using the pre-dispersion and preparation of the composition, can solve the problems of not being able to provide compression deformation properties, anti-aging properties, etc.

Inactive Publication Date: 2004-08-25
维平·夏尔马
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, studies have shown that this existing polymeric mixture does not provide the good compression set properties or good anti-aging properties needed to make predispersants for rubber chemicals

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0099] 2.5 kg of ethylene vinyl acetate (Grade 2825 provided by NATIONAL ORGANIC CHEMICALINDUSTRIES LTD., MUMBAI, India) containing 28% vinyl acetate and 5 kg of EPDM rubber (produced by DSMN.V., Netherlands) The supplied KELTAN GRADE No. 4802) was melt-mixed in a kneader (provided by EXTRUSION SYSTEMS, New Delhi, India). The polymer is melt-mixed in the kneader at 90°C for approximately 18-20 minutes. The resulting 1.5 kg polymer mixture was added to another mixer / kneader and 10 kg of sulfur and 1 kg of polyisobutylene (manufactured and manufactured by Gujarat Petrosynthesis Ltd.) were added to the mixer / kneader. Sold by Indian Petrochemicals Corporation Ltd., Vadodara, India, grade PV10). The sulfur complexing agent is milled in a nitrogen blanket to ensure that its particle size is 500-750 mesh before being added to the polymer mixture. The finally obtained mixture is melt-mixed in a kneader. Care must be taken to ensure that the treatment temperature does not exceed 56°C to pr...

example 2

[0101] Combine 0.5 kg of ethylene vinyl acetate (Grade 2825 provided by NATIONAL ORGANIC CHEMICALINDUSTRIES LTD., MUMBAI, India) with 28% vinyl acetate and 1 kg of PIB (KELTAN provided by DSM NV, Netherlands). GRADE No. 4802) was melt-mixed in a kneader (provided by EXTRUSION SYSTEMS, New Delhi, India). To the mixer / kneader were added 10 kg of sulfur and 1 kg of polyisobutylene (manufactured by Gujarat Petrosynthesis Ltd. and sold by Indian Petrochemicals Corporation Ltd., Vadodara, India, grade PV10).

[0102] The above-mentioned sulfur complexing agent has been ground in a nitrogen blanket to ensure that its particle size is 500-750 mesh. The mixture is melt-mixed in a kneader.

[0103] Care must be taken to ensure that the treatment temperature does not exceed 56°C to prevent harmful effects on the characteristics of the final pre-dispersion system.

[0104] The resulting rubber mud is fed to a pelletizer with refrigeration supply. In this way, particles that can flow freely wi...

example 3

[0106] 2.5 kg of vinyl vinyl acetate (EVA) containing 40% vinyl acetate (manufactured by Sumitomo CHEMICAL CO. Ltd., Osaka, Japan, and supplied by its agency M / S.Kemeff Value Additives in Mumbai, India) Grade Sumitate RB 11) and 5 kg of EPDM rubber (KELTAN GRADE No.4802 provided by DSM NV in the Netherlands) were melt-mixed in a kneader (provided by EXTRUSION SYSTEMS in New Delhi, India).

[0107] The polymer is melt-mixed in the kneader at 90°C for about 18-20 minutes to obtain a preliminary polymer mixture. The 1.5 kg polymer mixture obtained above was added to another mixer / kneader and 10 kg of sulfur and 1 kg of PIB (manufactured by Gujarat Petrosynthesis Ltd.) were added to the mixer / kneader. And the grade PV10 sold by Indian Petrochemicals Corporation Ltd., Vadodara, India. The above-mentioned sulfur is ground in a nitrogen blanket to ensure that its particle size is 500-750 mesh. The melt mixing reaction is carried out in a kneader.

[0108] Care must be taken to ensure tha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to view more

Abstract

The present invention relates to predispersions of rubber chemicals and to a process for the preparation thereof. The present invention also relates to a novel polymeric composition for dispersing a rubber chemical and to a process for the preparation of said composition.

Description

Invention field [0001] The invention relates to a pre-dispersion system of rubber additives and a method for preparing such rubber additives. The present invention also relates to a composition for dispersing rubber additives and a method for preparing the composition. Background of the invention [0002] It is well known that vulcanizing rubber is a step to enhance rubber characteristics such as robustness. In the rubber vulcanization process, a large number of rubber additives are used. These additives include: vulcanizing agents, such as sulfur; catalysts, such as ZnO; accelerators; retarders, etc. All these additives are in powder form. [0003] A method of vulcanizing diene rubber by heating together with sulfur and a vulcanization accelerator has been available for many years. In this way, a vulcanized rubber with certain physical properties can be obtained, such as higher tensile strength, elasticity and fatigue resistance. However, it can be said that this vulcanized rubb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J3/22
CPCC08J3/226C08J2421/00C08J2423/00C08J2321/00C08J3/22
Inventor 维平·夏尔马
Owner 维平·夏尔马
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap