Method for producing granular cryolite

A production method and cryolite technology, applied in the direction of die extrusion granulation, aluminum fluoride, aluminum halide, etc., can solve the problems that restrict the technological progress and healthy development of the aluminum electrolysis industry, unfavorable automatic blanking and environmental protection requirements, and large flying losses. and other problems, to achieve the effect of pure appearance color, low cost and less flying loss

Inactive Publication Date: 2004-09-29
DO FLUORIDE CHEM CO LTD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the progress of society and the development of aluminum electrolysis industry, the automation level of industrial production and environmental protection are getting more and more attention, and they need to be improved urgently. As the raw material of aluminum electrolysis - cryolite, its performance also needs to be improved, while the traditional Powdery cryolite and sandy cryolite have problems such as poor fluidity and high flying loss to varying degrees, which are not conducive to automatic cutting and environmental protection requirements, and to a large extent restrict the technological progress and healthy development of the world's aluminum electrolysis industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing granular cryolite
  • Method for producing granular cryolite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] Such as figure 1 As shown, the production method of the present invention comprises the following steps: first get the qualified cryolite, add the cryolite to the storage bin with the elevator, quantitatively add the cryolite to the feeding screw feeder by the star feeder; Adjust the situation, adjust the rotation frequency of the feeding screw in time, so that the cryolite enters the gap between the two rolls with a certain pressure. With the continuous operation of the rolls, the cryolite is extruded into flake materials, and the flake materials are crushed by the crusher. Enter the vibrating screen for screening and grading. Qualified granular materials are sent to the finished product post. The cryolite fine powder is sent back to the storage bin by the elevator for secondary granulation. The large cryolite is crushed by the granulator and sent to the finished product post.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The production process of granular cryolite and the cryolite is pelletized in a dry rolling pelletization apparatus. The cryolite produced in the method of the present invention has the following advantages: production under normal temperature, no decomposing of the product, high product quality stability, homogeneous and controllable grain size, high hardness, less breaking, pure color, low cost, low flying loss and high flowability. The produced cryolite is used mainly as flux in producing electrolyzed aluminum and has unique application superiority in automatic material feeding and protecting environment.

Description

technical field [0001] The invention relates to a production method of granular cryolite. Background technique [0002] The chemical name of cryolite is sodium fluoroaluminate, and the molecular formula is Na 3 AlF 6 , mainly used as a flux for aluminum electrolysis, wear-resistant filler for rubber and grinding wheels, opalescent agent for enamel, opacifier for glass and metal flux, etc. At present, cryolite mainly includes powdery cryolite and sandy cryolite. With the progress of society and the development of aluminum electrolysis industry, the automation level of industrial production and environmental protection are getting more and more attention, and they need to be improved urgently. As the raw material of aluminum electrolysis - cryolite, its performance also needs to be improved, while the traditional Powdery cryolite and sandy cryolite have problems such as poor fluidity and high flying loss to varying degrees, which are not conducive to automatic cutting and e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J2/22C01F7/54
Inventor 李世江侯红军杨华春皇甫根利刘慈军张富山连小闯
Owner DO FLUORIDE CHEM CO LTD