Die pressing and forming method for polytetrafluoroethylene thin wall crustose products flexible die

A polytetrafluoroethylene and compression molding technology, applied in the field of soft molding, can solve the problems of difficult conditions, leakage of sealed bags, contamination of products, complicated production equipment and processes, etc., and achieves high production efficiency, uniform internal quality, and product quality The effect of quality and yield improvement

Active Publication Date: 2004-11-10
中国航天科技集团公司第一研究院第七〇三研究所
View PDF0 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The PTFE products formed by hydraulic method are uniformly compressed, stable in size and good in quality, but require autoclave or high-pressure pump, high-pressure sealed bag and pressure t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Die pressing and forming method for polytetrafluoroethylene thin wall crustose products flexible die
  • Die pressing and forming method for polytetrafluoroethylene thin wall crustose products flexible die
  • Die pressing and forming method for polytetrafluoroethylene thin wall crustose products flexible die

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The present invention will be further described below in conjunction with accompanying drawing:

[0025] Such as Figure 1 to Figure 6 Shown is the first embodiment of the present invention---external pressure method, and concrete steps are as follows: (1) design and manufacture rigid mould, charging frock and appropriate thickness according to product size and the shrinkage rate of polytetrafluoroethylene (PTFE) The rubber or elastomer soft mold 1, the rigid mold includes product forming male mold 2, soft mold forming male mold 3, guide ring 4 and female mold 5, and the charging tooling includes charging core 6 and uniformly distributed 120° Three mold core positioning blocks 7; (2) according to product base thickness: base material ≈ 1: 5 (compression ratio) paving PTFE base material 8, three mold core positioning blocks 7-1, 7-2, 7-3 Place it on the guide ring 4 at 120°, put the charging core 6 in the center formed by them and touch the PTFE base material 8, and then...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention is a soft mode die forming method of teflon thin-wall shell product, using a definitely elastic soft mode to regulate and transfer molding pressure between a rigid mould and teflon powder, thus able to primely remedy inevitable nonuniformity during charging materials of teflon special-shaped pieces, overcoming the defect in molding teflon thin-wall shell products, radically improving product quality and yield, and unnecessary to add any new devices, liquid mediums and sealing bags.

Description

technical field [0001] The invention relates to a soft mold compression molding method, in particular to a soft mold compression molding method for polytetrafluoroethylene (abbreviated as PTFE) thin-wall shell-shaped products. Background technique [0002] At present, the common compression molding method for polytetrafluoroethylene thin-walled shell-shaped products is to pour polytetrafluoroethylene molding powder into a rigid cavity for compression. The size of the rigid cavity is usually designed according to the size of the product and the compression ratio of the material, but complex products bring great difficulties to the cavity design and loading process. Due to the poor fluidity of the material, the uniformity of the pressure distribution during the pressing process cannot be adjusted by the flow of the material, but can only be guaranteed by the uniformity of the charge. Therefore, the conventional molding method cannot adjust the pressure distribution and size of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C43/12B29C67/04
Inventor 姜卫陵郦江涛罗苹李德利
Owner 中国航天科技集团公司第一研究院第七〇三研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap