Vermiculizer for disposing high sulfur melted iron in vermicular cast iron production

A technology of vermicular graphite cast iron and vermicularizing agent, which is applied in the field of processing molten iron with high sulfur content, can solve the problems of restricting the production and use of vermicular graphite iron, difficult casting production, and large fluctuation of production, and achieves strong anti-recession ability, Stable creeping effect and stable response

Inactive Publication Date: 2004-11-10
HUAZHONG UNIV OF SCI & TECH
View PDF1 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Especially when the amount of sulfur in high-sulfur molten iron and molten iron fluctuates greatly, the fluctuation of productio

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0029] Example 1:

[0030] The chemical composition of the creeping agent: magnesium (Mg): 3%, rare earth (RE): 20%, silicon (Si): 42.5%, calcium (Ca): 2.5%, zinc (Zn): 1.5%, barium (Ba ): 1.0%, aluminum (Al): 1.0%, the remainder is iron (Fe).

[0031] Preparation method: Put 11% silicon calcium alloy (SiCa), 5% silicon barium alloy (SiBa) and 42% rare earth ferrosilicon alloy (RESiFe) into the bottom of the crucible, and then add 3% magnesium ingot, 1.0% aluminum ingot, and 1.5% zinc Then put the remaining 30% rare earth ferrosilicon alloy (RESiFe) and 6.5% ferrosilicon alloy (SiFe) on top of magnesium, aluminum, and zinc ingots, tamping and smelting. When the furnace temperature reaches about 1250~1300℃, the charge When it is completely liquid, stir it evenly and pour it into a metal ingot mold, and then crush it into a certain particle size after cooling.

Example Embodiment

[0032] Example 2:

[0033] The chemical composition of the vermicular agent: magnesium (Mg): 4%, rare earth (RE): 18%, silicon (Si): 43.5%, calcium (Ca): 2.0%, zinc (Zn): 1.0%, barium (Ba ): 1.5%, aluminum (Al): 1.5%, the remainder is iron (Fe).

[0034] Preparation method: Put 8.5% silicon calcium alloy (SiCa), 7.5% silicon barium alloy (SiBa) and 35% rare earth ferrosilicon alloy (RESiFe) into the bottom of the crucible, and then add 4% magnesium ingot, 1.5% aluminum ingot and 1.0% zinc Then put the remaining 30% rare earth ferrosilicon alloy (RESiFe) and 12.5% ​​ferrosilicon alloy (SiFe) on top of the magnesium, aluminum, and zinc ingots, tamping and smelting. When the furnace temperature reaches about 1250~1300℃, the charge When it is completely liquid, stir it evenly and pour it into a metal ingot mold, and then crush it into a certain particle size after cooling.

[0035] Example 1 of the effect of the present invention:

[0036] The RDS (Reciprocating Duplicate Systeem) nat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a creeping agent used for processing high-sulfur iron melt to produce vermicaular graphite cast iron, containing the components in weight percent: rare-earth (RE) 15-35%, magnesium (Mg) 2-6%, silicon (Si) 35-45%, aluminum (Al) 1-5%, calcium (Ca) 1-5%, zinc (Zn) 0.5-2.5%, barium (Ba) 0.5-2.5%, and iron (Fe) the rest. It is melted of the raw materials of rare-earth silicon iron alloy, metal Mg, SiCa, SiBa, Al ingot, Zn ingot, etc. The invention has the characters of simple operation, good solubility, stable reaction, high absorptivity, high creeping rate, stable creeping effect, and strong anti-decay ability, and can meet the requirements of producing casts at different wall thicknesses, has wide marketing prospect and remarkable economic benefits.

Description

technical field [0001] The invention relates to a vermicular agent for processing molten iron to produce vermicular graphite cast iron. Especially for the treatment of molten iron with high sulfur content. Background technique [0002] Graphite in vermicular graphite cast iron is worm-like, a graphite form between spherical graphite and flake graphite, and graphite is connected together in the eutectic group. The ferrite content in the as-cast structure of ordinary vermicular graphite cast iron is relatively high, and the amount of pearlite can be increased by alloying (Cr, Mo, Cu, Sn, Sb) or normalizing treatment. The tensile strength, elongation and impact toughness of compacted graphite cast iron are between gray cast iron and ductile iron. Both gray cast iron and gray cast iron are good, and can be used to manufacture steel ingot molds, exhaust pipes, glass molds, brake discs and other parts that work under alternating temperatures. The casting performance of vermicul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C33/08C22C33/10
Inventor 蔡启舟胡开华魏伯康
Owner HUAZHONG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap