A technology of sea-island fiber and production equipment, applied in the field of chemical fiber polyester processing, can solve the problems of rising production cost, increased capital investment, lack of competitiveness of products, etc., and achieve the effect of stable speed difference and excellent tension stability
Inactive Publication Date: 2004-12-08
厦门翔鹭化纤股份有限公司
View PDF0 Cites 11 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0007] Since the production of sea-island fiber POY and sea-island fiber FDY uses two different equipment and processing methods, it is undoubtedly difficult for manufacturers to use one set of equipment for the production of sea-island fiber POY and another set of equipment for the production of sea-island fiber FDY. Need to increase a lot of capital investment, resulting in increased production costs and products that lack competitiveness
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0025] see figure 1 Shown, a kind of sea-island fiber FDY production equipment of the present invention carries out the processing method of sea-island fiber POY production, it comprises;
[0026] Ordinary fiber-grade polyester chips are used as the first raw material A. After the raw material A is dried by the first dryer 11, it enters the first screw extruder 21 and is melted and extruded by the first screw extruder 21 to become a spinnable fiber. The polyester melt from the first screw extruder 21 is measured by the measuring head to ensure that the spinning temperature is 285-295°C, and after filtering, it is sent to the ordinary polyester melt by the melt distribution pipe. The spinning metering pump accurately measures, and the melt manifolds of equal length are evenly distributed to the corresponding composite components that are insulated by the spinning box 3;
[0027] Water-soluble polyester chips are used as the second raw material B. After the raw material B is dr...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
POY sea-island fibers can be produced by FDY sea-island apparatus from common fiber-grade polyester slices and aqueous soluble polyester slices as raw materials, which are respectively dried via a drying device, melted and injected via a screw injector to form spinnable molten of polyester, filtered, fed to a molten polyester distributor with metering pump for spinning, metered accurately, distributed to correspondent thermal composite assemblies with thermal spinning casings via molten feeding manifolds of with equal lengths, mixed there and sprayed out, laterally blown to cool, oil supplied via spinning channels and pre-network nozzles, and led to go through first and second heating rollers to be winded and form silk cakes of POY sea-island fibers. Both of the fibers can be produced in one apparatus to save investment.
Description
technical field [0001] The invention belongs to the technical field of chemical fiber polyester processing, and in particular relates to a processing method for producing sea-island fiber POY based on sea-island fiber FDY production equipment. Background technique [0002] Sea-island fiber is a kind of composite fiber. After post-processing and finishing, the composite fiber can be the thinnest commercialized fiber in the world. It is an ideal raw material for producing high-grade clothing fabrics, high-grade decorative cloths, and high-grade wiping materials. The sea-island fiber currently known in the industry is made of ordinary fiber-grade polyester chips (PET) as the island component, and a special polyester chip (ie, water-soluble polyester chip ES-CHIP) as the sea component. , Extruded and melted into the spinning metering pump with spinning box insulation for precise metering and extrusion, distributed to each composite spinning assembly, evenly distributed island co...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): D01D5/08D01D5/30D01F8/14
Inventor 陈耀南
Owner 厦门翔鹭化纤股份有限公司