N-acyl sarcosine modified aqueous magnetic liquid and its preparation method

A technology of acyl sarcosine and magnetic liquid, which is applied in the field of water-based magnetic liquid and its preparation, can solve the problems of poor dispersion of nanoparticles, thick outer coating layer, and easy agglomeration, and achieve good biocompatibility

A technology of acyl sarcosine and magnetic liquid, which is applied in the field of water-based magnetic liquid and its preparation, can solve the problems of poor dispersion of nanoparticles, thick outer coating layer, and easy agglomeration, and achieve good biocompatibility

CN1555910AInactive Publication Date: 2004-12-22SUN YAT SEN UNIV
0 Cites 4 Cited by

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • N-acyl sarcosine modified aqueous magnetic liquid and its preparation method
  • N-acyl sarcosine modified aqueous magnetic liquid and its preparation method
  • N-acyl sarcosine modified aqueous magnetic liquid and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Take 100g FeSO 4 .7H 2 O, formulated as FeSO with a mass concentration of 30% 4 solution, weighing 195gFeCl 3 .6H 2 O, formulated as FeCl with a mass concentration of 70% 3 solution, the two solutions are mixed according to the ratio of ferrous sulfate:ferric chloride (molar ratio)=1:1.5 to form an iron salt mixed solution. At the same time, add iron salt mixed solution and 450ml of ammonia water with a concentration of 25%, stir at high speed, adjust the rotation speed to 1300 rpm, and keep the reaction temperature at about 60°C for 10 minutes. To remove Cl - , SO 4 -2 and NH 4 + Etc., add 800ml distilled water in the reaction system under stirring condition after reaction finishes, continue to stir 3 minutes under stirring speed 400 revs / min, adopt magnetic seat settling to separate nano ferroferric oxide magnetic particle and supernatant liquid, carry out 3 times repeatedly Second-rate. Add a small amount of distilled water and 30ml of oleoyl sarcosine to ...

Embodiment 2

[0026] Take 100g FeSO 4 .7H 2 O, formulated as FeSO with a mass concentration of 15% 4 solution, weighing 195gFeCl 3 .6H 2 O, formulated as FeCl with a mass concentration of 60% 3 Solution, all the other steps are with embodiment 1. The saturation magnetization of magnetic liquid can reach 300 Gauss.

Embodiment 3

[0028] Take 100g FeSO 4 .7H 2 O, formulated as FeSO with a mass concentration of 20% 4 solution, weighing 195gFeCl 3 .6H 2 O, formulated as FeCl with a mass concentration of 65% 3 Solution, all the other steps are with embodiment 1. The saturation magnetization of magnetic liquid can reach 300 Gauss.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A N-acylsarcosine modified water-base magnetic liquid used as magnetic carrier to separate cell, protein and gene is prepared through synthesizing and washing magnetic nanoparticles, and using N-acylsarcosine as tabilizer to prepare magnetic liquid.

Description

technical field [0001] The invention relates to a water-based magnetic liquid and a preparation method thereof, in particular to an N-acyl sarcosine modified water-based magnetic liquid and a preparation method thereof. Background technique [0002] The so-called magnetic liquid refers to a stable colloidal system formed by highly dispersed nano-magnetic particles adsorbed with a stabilizer in a carrier liquid. It is mainly composed of nano magnetic particles, stabilizer and carrier liquid. At present, the preparation methods of water-based magnetic liquids can be divided into three categories according to the types of stabilizers used: 1) polymers with hydrophilic groups are used as stabilizers, and the stabilizers used are mainly polysaccharides, proteins, polymers, etc. Acrylic, polyacrylamide, etc., the current disadvantages of this type of water-based magnetic liquid are thick outer coating layer and low saturation magnetization; 2) Use water-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
22 Dec 2004
Publication
CN1555910A
IPC
B01J13/00
Inventors
徐雪青; 沈辉