Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Porcelain imitating paint

A technology for imitating porcelain paint and raw materials, applied in the field of imitating porcelain paint, can solve the problems of short service life, low surface hardness, easy to leave scratches, etc., and achieve the effects of long service life, long storage period and shortened construction period.

Inactive Publication Date: 2005-04-06
长春恩维物贸有限责任公司
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the imitation porcelain coatings produced in my country belong to calcium-plastic coatings and tempered coatings. The outer surface of this coating is like porcelain, smooth and smooth, luxurious and elegant, but it has disadvantages such as not being resistant to water washing, wet wiping off powder, etc., and the hardness of the finish is low. , easy to leave scratches, short shelf life, short service life, so users are not satisfied

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Embodiment 1 (unit is kilogram)

[0014] Polyvinyl alcohol 25 Calcium carbonate powder 320 Talc powder 28 Ash calcium powder 100 Wollastonite powder 26

[0015] Bentonite 40 Octanol 1.5 Hydroxyethyl Cellulose 2 OP-10 8 Dibutyl 1.0

[0016] Toluene 0.1 Urea 1.0 TP-1 anti-sedimentation agent 3 The rest is water

[0017] Production process: Add a certain amount of water and polyvinyl alcohol into the reactor, dissolve it into polyvinyl alcohol glue under heating and stirring, and lower it to the specified temperature, then add octanol, hydroxyethyl cellulose, OP-10 , dibutyl fat, toluene, urea, TP-1 anti-sedimentation agent, after stirring evenly, it becomes a mixed liquid of polyvinyl alcohol and chemical additives, and then released from the discharge port of the reactor into the container as the base material of the coating; Add a certain amount of base material into the reaction kettle, add calcium carbonate powder, talcum powder, lime calcium powder, wollastonite po...

Embodiment 2

[0018] Embodiment 2 (unit is kilogram)

[0019] Polyvinyl alcohol 34 Calcium carbonate powder 350 Talcum powder 32 Ash calcium powder 130

[0020] Wollastonite powder 32 Bentonite 60 Octanol 2.0 Hydroxyethyl cellulose 4 OP-10 10

[0021] Dibutyl fat 1.5 Toluene 0.15 Urea 1.5 TP-1 Anti-sedimentation agent 5 The rest is water

[0022] Production process: Add a certain amount of water and polyvinyl alcohol into the reactor, dissolve it into polyvinyl alcohol glue under heating and stirring, and lower it to the specified temperature, then add octanol, hydroxyethyl cellulose, OP-10 , dibutyl fat, toluene, urea, TP-1 anti-sedimentation agent, after stirring evenly, it becomes a mixed liquid of polyvinyl alcohol and chemical additives, and then released from the discharge port of the reactor into the container as the base material of the coating; Add a certain amount of base material into the reaction kettle, add calcium carbonate powder, talcum powder, lime calcium powder, wollast...

Embodiment 3

[0023] Embodiment 3 (unit is kilogram)

[0024] Polyvinyl alcohol 30 calcium carbonate powder 340 talcum powder 30 ash calcium powder 115 wollastonite powder 292

[0025] Bentonite 50 octanol 1.8 hydroxyethyl cellulose 3 OP-10 9 dibutyl fat 1.2

[0026] Toluene 0.15 Urea 1.2 TP-1 anti-sedimentation agent 4 The rest is water

[0027] Production process: Add a certain amount of water and polyvinyl alcohol into the reactor, dissolve it into polyvinyl alcohol glue under heating and stirring, and lower it to the specified temperature, then add octanol, hydroxyethyl cellulose, OP-10 , dibutyl fat, toluene, urea, TP-1 anti-sedimentation agent, after stirring evenly, it becomes a mixed liquid of polyvinyl alcohol and chemical additives, and then released from the discharge port of the reactor into the container as the base material of the coating; Add a certain amount of base material into the reaction kettle, add calcium carbonate powder, talcum powder, lime calcium powder, wollast...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

One kind imitates the porcelain coating, is by the polyvinyl alcohol, the calcium carbonate powder, the talcum powder, the ash calcium powder, the wollastonite powder, the bentonite, the zinc mellow, the ethylol cellulose, Op-10, the dibutyl ester, the toluene, the urea, Tp-1 guards against sinks the medicinal preparation, the water mix is made, the degree of hardness high, the smooth finish good, bears scours, the product storage time long, the ventilation moisture-proof, the service life long, the application scope is broad, may cause the architectural engineering to reduce the time limit for a project.

Description

Technical field: [0001] The invention belongs to building materials, in particular to a porcelain-like paint. Background technique: [0002] At present, the imitation porcelain coatings produced in my country belong to calcium-plastic coatings and tempered coatings. The outer surface of this coating is like porcelain, smooth and smooth, luxurious and elegant, but it has disadvantages such as not being resistant to water washing, wet wiping off powder, etc., and the hardness of the finish is low. , easy to leave scratches, short shelf life, short service life, so users are not satisfied. Invention content: [0003] The technical problem to be solved by the present invention is to provide an imitation porcelain coating with high hardness, good smoothness, scrub resistance, long product storage period, breathable and moisture-proof, long service life and wide application range, which can shorten the construction period of construction projects. [0004] The present invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/28C09D129/04
Inventor 周涛
Owner 长春恩维物贸有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.