A technology of ultraviolet light and inkjet printer, applied in the directions of ink, application, household appliances, etc., can solve the problems of flammability, toxicity, environmental pollution, etc., and achieve the effect of satisfying high-speed printing, wide adaptability, and good development prospects

Inactive Publication Date: 2005-06-29
DONGHUA UNIV
View PDF1 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The biggest disadvantage of solvent-based inks is the pollution to the environment. Because most organic solvents have problems such as

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Aliphatic polyurethane acrylate prepolymer (CN964 Sartomer company) 7.5 grams

[0028] Monofunctional monomer (ethoxyethoxyethylacrylate) 28g

[0029] Monofunctional monomer (tetrahydrofuran acrylate) 20 grams

[0030] Difunctional monomer (1,6 hexanediol diacrylate) 25 grams

[0031] Trifunctional monomer (trimethylolpropane triacrylate) 10g

[0032] Pigment Red 185 (Fast Magenta S4C Jiaozhou Fine Chemical Company) 2.8g

[0033] CH-13B Hyperdispersant (Shanghai Sanzheng Polymer Material Co., Ltd.) 1.5g

[0034] Photoinitiator Irgacure 369 (Ciba, USA) 5.0 grams

[0035] Fluorosurfactant FC430 (US 3M Company) 0.2 grams

[0036] The grinding and dispersing process uses the ZETA experimental grinder from NETZSCH, and the mixing process uses the experimental emulsifier from Shanghai Weiyu Electromechanical Manufacturing Co., Ltd. The grinding time is 2-4 hours, and the stirring is at 8000 rpm Under the speed of rotation, the stirring time is 30-60 minutes. The test r...

Embodiment 2

[0038] Aliphatic urethane acrylate prepolymer (EB270 UCB Company) 16.7 g

[0039] Ethoxy ethoxy ethyl acrylate 40g

[0040] 1,6 hexanediol diacrylate 24g

[0041] Trimethylolpropane Triacrylate 12g

[0042] Pigment Red 185 (Fast Magenta S4C Jiaozhou Fine Chemical Company) 2.0g

[0043] Hyperdispersant SOLSPERSE 22000 (Avecia company) 1.0 grams

[0044] Photoinitiator Irgacure 819 (Ciba, USA) 4.0 grams

[0045] Fluorosurfactant FC430 (US 3M Company) 0.3 grams

[0046] The same preparation method as in Example 1, the test results are shown in Table 2

Embodiment 3

[0048] Aliphatic urethane acrylate prepolymer (PHOTOMER6010) 12g

[0049] Ethoxy ethoxy ethyl acrylate 20g

[0050] THF acrylate 21g

[0051] 1,6 hexanediol diacrylate 20g

[0052] Trimethylolpropane Triacrylate 16g

[0053] Pigment Red 185 (Fast Magenta S4C Jiaozhou Fine Chemical Company) 3.0g

[0054] CH-13B Hyperdispersant (Shanghai Sanzheng Polymer Material Co., Ltd.) 1.7g

[0055] Photoinitiator Irgacure 369 (Ciba, USA) 6.0 grams

[0056] Fluorosurfactant FC430 (US 3M Company) 0.3 grams

[0057] The same preparation method as in Example 1, the test results are shown in Table 2

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Disclosed are components of a ultraviolet ray solidified printing ink for digital spraying machine and its preparing method. The UV solidified printing ink comprises of prepolymer, active monomer, color, photoinitiator, dispersant and surface active agent, which are mixed by a certain ratio, through grinded ( instantaneously ) and stirring to produce the product. The printing ink doesn't contain organic solvent, for environmental protection, it can be solidified in grinded ( instantaneously ) under the ultraviolet ray for satisfying high speed requirement, as well as print on glass steel,PE and PP film, eramic tile and film and other material, with wide application and bright future.

Description

technical field [0001] The invention relates to an ultraviolet (UV) curing ink and a preparation method thereof, in particular to a UV curing ink applied on a digital flat-panel inkjet printer and a preparation method thereof. Background technique [0002] In recent years, large-scale inkjet printers have developed rapidly with the development of the computer industry. According to the working principle of the nozzle, inkjet printers can be divided into thermal foam type and piezoelectric crystal type. Thermal foam nozzles are mainly used in inkjet printers produced by Hewlett-Packard, Mimaki and other companies. These machines mainly use water-based inks, and the colorants are usually dyes; , Shenyang Airship and other companies' inkjet printers, this type of nozzle mainly uses solvent-based inks, and the colorant is organic pigments. As the requirements for environmental protection are getting higher and higher, nozzles using UV-curable inks have begun to appear and have ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/30
Inventor 王夏琴李文彬
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap