An epoxy adhesive and nano-powder technology, applied in the direction of adhesive, epoxy resin glue, adhesive type, etc., can solve the problems of complex process, environmental pollution, high cost, and achieve simple modification process, good comprehensive performance, easy to use effect of operation

Inactive Publication Date: 2005-11-09
ZHEJIANG UNIV
View PDF10 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, the above methods require related equipment, solvents, etc., chemical reactions occur, the process is complex, and the cost is high, resulting in environmental pollution
[0007] There are also reports on the introduction of inorganic nanoparticles into e

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] Example 1:

[0017] Weigh 0.3Kg of A component in the German Henkel epoxy adhesive (Pattex® Henkel Black & Decker), and add 6 g of nano SiO 2 , Uniformly mechanically mix, add 0.3Kg of component B, mix evenly, clean and blow dry the steel sheet polished with 150# metallographic sandpaper with acetone, and apply the nano-mixed adhesive on the two steel sheets. The pieces are glued together and cured in an oven at 50°C for 1 hour. Compared with unmodified, the drawing strength is increased by 3.3 times.

Example Embodiment

[0018] Example 2:

[0019] Weigh 0.4Kg of component B in Guanwei Super Epoxy EPO-530 epoxy adhesive, and add 8g of nano Al 2 O 3 , Mechanically stir and mix evenly, then add 0.4Kg of component A, the process is the same as in Example 1. The shear strength is doubled compared with the unmodified one.

Example Embodiment

[0020] Example 3:

[0021] 2g of nano Al 2 O 3 Put it in 140g of acetone, ultrasonically shake for 30-60 minutes, then mix with 0.2Kg of component A in Guanwei® SuperEpoxy EPO-530 epoxy adhesive, vortex the solvent for 10 minutes at 70℃, and add 0.2Kg of For component B, the process is the same as in Example 1. Its shear strength is 60% higher than that of unmodified.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A nanoparticles modified epoxy adhesive for ceramics, metals and high-molecular materials is proportionally prepared from the dual-component epoxy adhesive and nanoparticles through mechanical mixing or solution mixing.

Description

technical field [0001] The invention relates to a preparation method of nano powder modified epoxy adhesive. Background technique [0002] The application of adhesives, especially epoxy adhesives, has been extended to many fields, providing an effective way for all walks of life to simplify processes, save energy, reduce costs, and improve economic benefits, and is increasingly replacing mechanical connections. However, general adhesives have low bonding strength and can only meet the needs of general bonding strength in daily life and engineering. [0003] Epoxy adhesives with epoxy resin as the main component have excellent mechanical properties, water resistance, aging resistance, chemical medium resistance, good acid and alkali resistance, and good bonding performance, so they are suitable for epoxy resins. The modification of the adhesive mostly focuses on improving the brittleness of the epoxy resin adhesive, toughening it (Chinese patent 03135153.0, 03117022.6, 03112...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J163/00
Inventor 凌国平翟兰兰栾飞毛启楠郑一方
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap