Method for producing black transparent microcrystal glass and its products

A glass-ceramic and transparent technology, which is applied in the field of Li2O-Al2O3-SiO2 black transparent glass-ceramics, can solve the problems of unpublished and undiscovered patent bulletins, and achieve the advantages of improved service life, long service life and high strength Effect

Active Publication Date: 2005-11-23
广东科迪微晶玻璃实业有限公司 +1
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, various heating products produced by glass ceramics have not been found in the market, such as heating plates, pans, grilling plates, frying pans, etc. for induction cookers, microwave ovens, Yale stoves, gas stoves, etc. its related content

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: the production method of black transparent glass-ceramic heating plate, frying plate, its technological process comprises:

[0023] (1) batching; the weight percentage of each raw and auxiliary material is: Li 2 O: 3.1%; CaO: 2.2%; Al 2 o 3 : 20%; SiO 2 : 68.8%; NiO: 0.07%; V 2 o 5 : 0.14%; Fe 2 o 3 : 0.09%; TiO 2 : 2.0%; ZrO 2 : 1.8%; P 2 o 5 : 1.8%; (2) mixing; (3) melting, carried out in a glass melting furnace to make it melt, and the melting temperature is 1610 ° C; (4) cooling; (5) calendering, the temperature is 1320 ° C; (6 ) annealing, at this time the color of the glass plate is light brown; (7) crystallization treatment, the temperature is 840 ° C, and the time is 2 hours, at this time the color of the glass becomes black and transparent; (8) cutting the plate, according to (9) Grinding and polishing; (10) Trimming; (11) Inspection; (12) Printing, such as printing trademarks, logos, etc.; (13) Drying; (14) Finished product inspection;...

Embodiment 2

[0025] Embodiment 2: the production method of black transparent glass-ceramic heating plate, its technological process comprises: (1) batching; The weight percentage of each raw and auxiliary material is: Li 2 O: 3.7%; MgO: 2.5%; Al 2 o 3 : 22.5%; SiO 2 : 66%; NiO: 0.09%; V 2 o 5 : 0.13%; Fe 2 o 3 : 0.08%; TiO 2 : 1.8%; ZrO 2 : 2%; P 2 o 5 : 1.2%; (2) mixing; (3) melting, carried out in a glass melting furnace to melt, the melting temperature is 1625 ° C; (4) cooling; (5) using heating plate molds and equipment, pressing molding, The temperature is 1330°C; (6) annealing, the color of the glass is light brown at this time; (7) crystallization treatment, the temperature is 830°C, and the time is 2.5 hours, at this time the color of the glass becomes black and transparent; ( 8) trimming; (9) inspection; (10) printing, such as printing trademarks, logos, etc.; (11) drying; (12) inspection of finished products; (13) packaging; (14) storage.

[0026] The black transparent...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for producing black transparent microcrystal glass and its products, wherein the base glass comprises Li2O, RO, Al2O3 and SiO2, the coloring agent comprises NiO, V2O5 and Fe2O3, the crystal nucleus agent comprises TiO2, Zr2O5 and P2O5, the weight percentage of each component being, Li2O: 2.5-4.7%, RO: 2-3%, Al2O3: 17-26%, SiO2: 62-72%, NiO: 0.05-0.1%, V2O5: 0.1-0.2%, Fe2O3: 0.05-0.1%, TiO2: 2-2.5%, ZrO2: 1.5-2.5%, P2O5: 1-2%. The formulation and related die arrangement can be used for making electromagnetic oven plate, disc, microwave oven disc, roasting and grilling plate, baking oven cloche, frying pan and various pots.

Description

Technical field: [0001] The present invention relates to Li 2 O-Al 2 o 3 -SiO 2 The composition of black transparent glass-ceramic and the production method of its products. Background technique: [0002] There are many types of glass-ceramics, and glass products for different purposes can be produced by different composition ratios and different processes. Most of the glass-ceramics disclosed in the patent literature are architectural decorative materials such as wall tiles, or handicraft products. At present, various heating products produced by glass-ceramics have not been found in the market, such as heating plates, pans, grilling plates, frying pans, etc. for induction cookers, microwave ovens, Yale stoves, gas stoves, etc. its related content. Invention content: [0003] The purpose of the present invention is to improve the existing glass-ceramic formula, and to provide a heating plate, pan, frying pan, frying pan and various heat-resistant pots suitable for i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C10/00C03C10/02
CPCC03C10/0027C03C10/0036C03C10/0054
Inventor 赵天佑庄堆业蔡来吉
Owner 广东科迪微晶玻璃实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap