Precisely pressed optical glass

A kind of optical glass, precise technology, applied in the field of optical glass, can solve the problems of poor glass devitrification resistance, unfavorable batch production, poor glass transmittance, etc., to achieve good devitrification resistance, excellent transmittance, liquid The effect of low phase temperature

Active Publication Date: 2006-05-17
CDGM OPTICAL GLASS
View PDF1 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Japanese patent publication 2577794 discloses a kind of ZnO-B 2 o 3 -Nb 2 o 5 -SiO 2 System precision pressed glass, but the zinc-boron system glass has poor devitrification resistance and is easy to react with corundum refractory materials, which is not conducive to mass production
[0007] CN95103393.X provides a SiO 2 -TiO 2 -ZrO 2 -K 2 O-RO (R stands for alkaline earth metal) optical glass, but the glass contains more TiO 2 , so the transmittance of the glass in the short-wave band region is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] SiO 2 Is the main component of glass, SiO 2 It can increase the viscosity of glass and improve the resistance to devitrification of glass. When its content is less than 8%, the transmittance and devitrification resistance of the glass are poor, and if it exceeds 30%, the refractive index of the glass decreases.

[0012] B 2 o 3 It is an essential component of glass. When its content is lower than 6%, the melting performance of the glass is poor, and the devitrification resistance is not ideal. If it is higher than 25%, the softening temperature of the glass is high.

[0013] ZnO is beneficial to reduce the softening temperature of the glass. When the content of ZnO is less than 8%, the softening temperature of the glass is high. If it is higher than 30%, the crystallization tendency of the glass increases.

[0014] Nb 2 o 5 It can increase the refractive index of the glass. When the content is lower than 0.5%, the transmittance of the glass is poor. When the conte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
transition temperatureaaaaaaaaaa
transition temperatureaaaaaaaaaa
Abbe numberaaaaaaaaaa
Login to View More

Abstract

The present invention provides one kind of precisely pressed optical glass. The optical glass consists of SiO2 8-30 wt%, B2O3 6-25 wt%, ZnO 8-30 wt%, Nb2O5 0.5-19 wt%, BaO 5-26 wt%, Li2O 0.5-7 wt% and ZrO2 1-6 wt% chemically. The optical glass of the present invention has refractivity of 1.65-1.74, Abbe number of 36-45, conversion temperature lower than 500 deg.c, high chemical stability, low liquid phase temperature, high devitrification resistance, high light permeability and low specific weight, and is especially suitable for precise mold pressing to form aspherical lens, spherical lens and other optical elements.

Description

Technical field [0001] The invention relates to an optical glass, in particular to an optical glass with a refractive index of 1.65-1.74 and an Abbe number of 36-45. The glass is suitable for precision molding of aspherical lenses and other optical elements. technical background [0002] With the fierce competition and development in the optoelectronic product market, high-volume production and low-cost manufacturing of optical components is the goal of every optical material and optical component manufacturer. The use of precision molding technology (including direct compression method and secondary compression method) can reduce raw material consumption, greatly reduce the amount of mechanical processing of optical components, thereby reducing labor and material costs, and can achieve stable batch production, while also reducing environmental pollution. On the other hand, with the increasing popularity of digital cameras, digital camcorders and camera phones in recent yea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/066
Inventor 匡波
Owner CDGM OPTICAL GLASS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com