Mixture for the production of an amber glass, amber glass, method for the production of tubes and blanks of tinted bulbs, and tinted bulbs obtained with said glass

A production method and mixture technology, applied in the production of amber glass blanks and/or tubes, in the field of amber glass, can solve the problems of small pieces of coating falling off, cracking and falling off, and color fade

Active Publication Date: 2007-02-14
JWF公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0020] As it ages, the color will fade significantly, and repeated thermal sho

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mixture for the production of an amber glass, amber glass, method for the production of tubes and blanks of tinted bulbs, and tinted bulbs obtained with said glass
  • Mixture for the production of an amber glass, amber glass, method for the production of tubes and blanks of tinted bulbs, and tinted bulbs obtained with said glass
  • Mixture for the production of an amber glass, amber glass, method for the production of tubes and blanks of tinted bulbs, and tinted bulbs obtained with said glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0106] The glass substrate is of the silicon-sodium-calcium type, and the main components are as follows:

[0107] SIO2: 65-72% (weight percent)

[0108] B2O3: 0.5-3%

[0109] Na2O: 5-15%

[0110] K2O: 5-15%

[0111] LiO2: 0.2-2%

[0112] CaO: 1-5%

[0113] MgO: 0.2-2%

[0114] SrO: 2-7%

[0115] BaO: 0.5-4%

[0116] Al2O3: 0.5-3%

[0117] MoO3: 0.05-0.5%

[0118] SO3: 0.1-0.7%

[0119] Oxides of elements such as iron, titanium, magnesium and zirconium Fe2O3, TiO2, MgO, ZrO2, etc. are present in small amounts (not intentionally added impurities).

[0120] On this basis, the average physical properties of the glass obtained are as follows, and the English terms currently used for these parameters are retained:

[0121] Melting point ("Melting point"): (log η=2) 1360°

[0122] Sampling point ("Gob point"): (log η=3) 1110°

[0123] Softening point ("Softening point"): (Littleton log η=7.6) 675°

[0124] Annealing point ("Annealing point"): (log η=13) 515°

[0125] Tg...

Embodiment 2

[0129] This substrate can be advantageously adapted to soda-lime glass commonly found in the low-cost lighting fixture industry, which provides the following ratios

[0130] SIO2: 68-72% by weight

[0131] Na2O: 12-16%

[0132] K2O: 0.5-1.5%

[0133] LiO2: 0.2-1%

[0134] CaO: 6-9%

[0135] MgO: 0.2-2%

[0136] BaO: 0.5-2%

[0137] SrO: 2-7%

[0138] BaO: 0.5-4%

[0139] Al2O3: 1-3%

[0140] MoO3: 0.05-0.5%

[0141] SO3: 0.1-0.7%

[0142] Elements such as Fe2O3, TiO2, ZrO2, etc. are also present in small amounts (impurities).

[0143] The average physical characteristics of the glass are thus as follows:

[0144] Melting point ("Melting point"): (log η=2) 1390°

[0145] Sampling point ("Gob point"): (log η=3) 1140°

[0146] Softening point ("Softening point"): (log η=4) 975°

[0147] Annealing point ("Annealing point"): (log η=7.6) 695°

[0148] Tg(log η=13): 530°

[0149] Quenching point ("Strain point"): (log η=13.3) 503°

[0150] Δ1 from 20 to 300°=10-7°C-1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Softening pointaaaaaaaaaa
Tgaaaaaaaaaa
Softening pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to a mixture for the production of amber glass colored in bulk, an amber glass obtained from said vitrifiable mixture based on a silicon-sodium-calcium composition and a method for the production of such glass Method for tube and blank 2 for bulb 1 . The mixture comprises 0.01% to 1% by weight of molybdenum disulfide and 0.01% to 7% by weight of strontium sulfide relative to 100% by weight of the mixture. The glass thus obtained is free of harmful products such as cadmium, and it is obtained without additional heat treatment for obtaining the desired color.

Description

technical field [0001] The invention relates to a vitrifiable mixture based on a silicon-sodium-calcium composition for obtaining amber glass colored in bulk. [0002] The invention also relates to this glass and to a method for producing amber glass blanks and / or tubes, as well as products such as said tubes or bulbs obtained using said blanks. Background technique [0003] “Amber” is understood to mean the colors from yellow to orange defined, for example, by international standards, in particular in the reference system of the International Commission on Illumination known under the name CIE 1931 . [0004] This is because the International Commission on Illumination has formulated the color standard for vehicle light through the SAE J578 standard, and the amber boundary is as follows: [0005] For red border y=0.390 [0006] For white border y=0.79-0.67x [0007] For the green border y=x-0.12. [0008] This can be shown by the enlarged first quadrilateral, the graphi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C1/02C03C1/00C03B9/14H01K1/28C03C1/10C03B9/18C03C3/091C03C4/02
CPCC03C4/02C03B9/18C03C1/00C03C1/022C03C1/10C03C3/091H01K1/28C03C3/076C03C3/085C03C3/11
Inventor C·勒菲弗F·勒佩斯科尔克斯
Owner JWF公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap