Method for directly electrodepositing zinc on magnesium surface

A magnesium alloy and electrodeposition technology, which is applied in the field of metal material surface treatment, can solve the problems of high process cost, complex process, and inability to realize large-scale industrial production, and achieve low cost, low price, and corrosion-free electroplating. Effect

Inactive Publication Date: 2007-03-28
SHANGHAI UNIV
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] In view of the shortcomings of the existing magnesium alloy surface treatment process, such as high cost and complicated process, the surface treatment of magnesium alloy has not been able to realize large-scale industrial production so far.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Put deionized water in a plastic beaker, then electromagnetically stir the deionized water at 200rpm, then put 10g / L zinc fluoride into the stirred deionized water.

[0028] (2) Sodium citrate, potassium sodium tartrate and EDTA complexing agent were respectively added to the above-mentioned stirred zinc fluoride suspension until all the zinc fluoride was dissolved and the zinc fluoride suspension became a clear solution.

[0029] (3) Add water-soluble benzylidene acetone and surfactant to the above-mentioned clear solution zinc fluoride solution.

[0030] (4) The small piece of AZ91D magnesium alloy sheet is pretreated by polishing and degreasing.

[0031] (5) Put the pretreated magnesium alloy into the above-mentioned clarified solution of zinc fluoride for electrodepositing zinc, and the density of the DC power supply is controlled at 0.5-2A / dm 2 , Electrolysis temperature 45-55 ℃.

[0032] (6) Finally, put the zinc-electrodeposited magnesium alloy into a heat ...

Embodiment 2

[0033] Embodiment 2, 3 methods are identical with embodiment 1, and process condition and effect are as follows

[0034] implement

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a magnesium alloy surface directly electrodeposited zinc method that includes the following steps: electrodepositing a layer of zinc on the magnesium alloy surface as protecting layer, adding complex agent into zinc fluoride deionized water until the suspension liquid becoming clear, putting the alloy into the solution to take electrodepositing zinc and putting the magnesium alloy to take thermal process in furnace. The method could realize industrialization producing and have no pollution to environment.

Description

technical field [0001] The invention relates to a method for surface treatment of metal materials, in particular to a method for surface treatment of magnesium alloys. Background technique [0002] Magnesium is the lightest metal structural material. Magnesium alloys have attracted much attention due to their small volume and mass, high specific strength, good processability, good electromagnetic shielding, and good vibration reduction, electrical and thermal conductivity. Magnesium alloys have developed greatly since they were used in the aerospace industry in the early days to the current applications in automotive materials, optical instruments, electronic telecommunications, and military industries. But the chemical stability of magnesium is low, the electrode potential is very negative (-2.34V), and the corrosion resistance is poor, which restricts the wide application of magnesium alloy materials to some extent. Therefore, the surface treatment of magnesium alloys and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25D3/22C25D5/30
Inventor 朱萍周鸣吴金华李坤芳周劲
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap