A technology for protecting films and polarizers, applied to polarizing elements, electronic equipment, applications, etc., can solve problems such as low productivity, floating or stripes, and insufficient polarization characteristics, and achieve high productivity, good polarization characteristics, and good appearance. Effect

Inactive Publication Date: 2007-04-18
NITTO DENKO CORP +1
View PDF8 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in this method, when the protective film and the polyvinyl alcohol-based polarizer are bonded, floating or streaks appear, the appearance is unstable, the polarization characteristics are not sufficient, and there is also a problem of low productivity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polarizer protecting film, polarizing plate and image display
  • Polarizer protecting film, polarizing plate and image display
  • Polarizer protecting film, polarizing plate and image display

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0108] (polarizer)

[0109] A polyvinyl alcohol film having a thickness of 80 μm was dyed in a 5% by weight (weight ratio: iodine / potassium iodide=1 / 10) iodine aqueous solution. Next, it is immersed in an aqueous solution containing 3% by weight of boric acid and 2% by weight of potassium iodide, and then stretched to 5.5 times in an aqueous solution containing 4% by weight of boric acid and 3% by weight of potassium iodide, and then dipped to 5% by weight. % potassium iodide aqueous solution. Subsequently, drying was performed for 3 minutes in a drying oven at 40° C. to obtain a polarizer having a thickness of 3 μm.

[0110] (Production of protective film with nylon-based resin)

[0111] To three extruders connected to the T-die head and set at a temperature of 250° C., cyclic olefin-based resins (manufactured by TICONA, Topas 6013) and adhesive resins (Mitsui Chemicals ( Co., Ltd., Adoma-PF508), nylon resin dried at 90°C for 5 hours (Ube Industries, Ltd., UBE5023B), after...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

Disclosed is a polarizer protecting film wherein a resin layer containing a nylon resin is arranged on a thermoplastic resin layer having a water vapor permeability of not more than 100 g / m<2> / 24h. Such a polarizer protecting film has good adhesion to the polarizer when it is bonded to a polarizer via an adhesive layer for producing a polarizing plate, and enables to obtain a polarizing plate having excellent polarizing characteristics.

Description

technical field [0001] The present invention relates to a polarizer protective film and a polarizer using the protective film. The polarizing plate can be used alone or as an optical film laminated with the polarizing plate to constitute an image display device such as a liquid crystal display device, an organic EL display device, or a PDP. Background technique [0002] For example, in a liquid crystal display device or the like, it is indispensable to arrange polarizing plates on both sides of a glass substrate that forms the surface of a liquid crystal panel due to its image forming method. A polarizer is generally used in which a protective film is bonded to both sides of a polarizer made of a polyvinyl alcohol-based film and a dichroic material such as iodine with a polyvinyl alcohol-based adhesive. , Triacetyl cellulose and the like are used in the protective film. [0003] However, triacetyl cellulose does not have sufficient heat and humidity resistance, and when a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G02B5/30B32B27/34G02F1/1335B32B7/02B32B7/12B32B27/08
CPCG02B5/30B32B7/12G02B1/105G02F1/133528G02B5/3025B32B27/08G02B1/14G02F1/1335B32B27/34B32B27/325B32B2307/42B32B2457/206B32B2457/204B32B2457/202
Inventor 辻内直树西田昭博与田健治江原启悟栗栖洋武居芳树每田知正
Owner NITTO DENKO CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap