Zinc comprising nanoparticles and related nanotechnology

a technology of nanoparticles and zinc, applied in the field of submicron and nanoscale powder manufacturing methods comprising zinc, to achieve the effect of high volum

Inactive Publication Date: 2005-06-16
PPG IND OHIO INC
View PDF24 Cites 74 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0013] In some embodiments, the present invention is methods for producing novel...

Problems solved by technology

Furthermore, since they represent a whole new family of material precursors where conventional coarse-grain physiochemical mechanisms are not...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zinc comprising nanoparticles and related nanotechnology
  • Zinc comprising nanoparticles and related nanotechnology

Examples

Experimental program
Comparison scheme
Effect test

examples 1-2

Zinc Oxide Powders

[0117] 99 weight % by metal pure zinc ethylhexanoate precursor was diluted with hexane until the viscosity of the precursor was less than 100 cP. This mix was sprayed into a thermal plasma reactor described above at a rate of about 50 ml / min using about 50 standard liters per minute oxygen. The peak temperature in the thermal plasma reactor was above 3000 K. The vapor was cooled to nucleate nanoparticles and then quenched by Joule-Thompson expansion. The powders collected were analyzed using X-ray diffraction (Warren-Averbach analysis) and BET. It was discovered that the powders had a crystallite size of less than 50 nm and a specific surface area of about 10 m2 / gm.

[0118] Next, in a separate run with the same process, the mix was sprayed at a rate of about 50 ml / min using about 65 standard liters per minute oxygen. The peak temperature in the thermal plasma reactor was above 3000 K. The vapor was cooled and then quenched by Joule-Thompson expansion. The powders c...

examples 3

Nickel Zinc Ferrite Powders

[0120] A mixture of nickel, zinc, and iron organometallic (octoates, 1:1:2::Ni:Zn:Fe ratios) precursor was prepared. Using the process of Example 1, the mixture was processed at a peak temperature exceeding 2000 K, and the powder was collected. The powders were characterized using X-ray diffractometer and 10 point BET surface area analyzer. The powders were found to be nickel zinc ferrite nanoparticles. No independent peaks of zinc, nickel, or iron oxide were observed suggesting lattice level mixing of atoms. The powders were of a brown color, and had a mean crystallite size less than 15 nanometers and a surface area greater than 40 m2 / gm. The powders were found to be magnetic.

[0121] This example shows that color pigment nanoparticles can be prepared from zinc and that complex three metal oxide nanoparticles can be produced.

example 4

Aluminum doped Zinc Oxide Powders

[0122] A mixture of aluminum and zinc organometallic precursors were prepared. The ratio was adjusted between the two metal precursors to achieve 1.5 wt % aluminum oxide and 98.5 wt % zinc oxide. Using the process of Example 1, the mixture was processed at a peak temperature exceeding 2000 K, and the powder was collected. The powders were characterized using X-ray diffractometer and 10 point BET surface area analyzer. The powders were found to be doped zinc oxide nanoparticles. No independent peaks of zinc or aluminum oxide were observed suggesting lattice level mixing of atoms. The powders had a mean crystallite size of about 25 nanometers and a surface area of about 20 m2 / gm. Electrical conductivity of zinc oxide from Example 1 and aluminum-doped zinc oxide from this example were measured. It was discovered that the doped zinc oxide was over 10 times more conductive than the pure zinc oxide nanopowder.

[0123] This example shows that electrically c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Electrical conductivityaaaaaaaaaa
Compositionaaaaaaaaaa
Electrical conductoraaaaaaaaaa
Login to view more

Abstract

Nanoparticles comprising zinc, methods of manufacturing nanoparticles comprising zinc, and applications of nanoparticles comprising zinc, such as electrically conducting formulations, reagents for fine chemical synthesis, pigments and catalysts are provided.

Description

CROSS-REFERENCE TO RELATED PATENT APPLICATIONS [0001] This application is a An application claiming the benefit under 35 USC 119(e) U.S. Application 60 / 449,626, filed Feb. 24, 2003, incorporated herein by reference in its entirety.FIELD OF THE INVENTION [0002] The present invention relates to methods of manufacturing submicron and nanoscale powders comprising zinc and applications of such powders. RELEVANT BACKGROUND [0003] Nanopowders in particular and sub-micron powders in general are a novel family of materials whose distinguishing feature is that their domain size is so small that size confinement effects become a significant determinant of the materials' performance. Such confinement effects can, therefore, lead to a wide range of commercially important properties. Nanopowders, therefore, are an extraordinary opportunity for design, development and commercialization of a wide range of devices and products for various applications. Furthermore, since they represent a whole new f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C1/04C22C18/00
CPCB82Y30/00C01G9/00C01G9/02C01G53/006C01P2002/52C01P2002/72C01P2002/60C01P2004/64C01P2006/12C01P2006/40C01P2006/80C09C1/04C22C18/00C01P2004/54
Inventor YADAV, TAPESH
Owner PPG IND OHIO INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap