Polyhydroxyalkanoate-containing structure and manufacturing method thereof

a technology of polyhydroxyalkanoate and manufacturing method, which is applied in the direction of transferases, instruments, applications, etc., can solve the problems of shortening the turnaround time, and achieve the effect of immobilizing a pha synthas

Inactive Publication Date: 2005-09-22
CANON KK
View PDF9 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0017] The present invention can effectively immobilize a PHA synthase on the surface of a base material, and so when a synthesis reaction is conducted by the addition of a 3-hydroxyacyl coenzyme A, no isolated PHA granules are generated, which can effectively coat the base material surface with the PHA.

Problems solved by technology

In addition, although conventional, organic, synthetic chemical methods requires a manufacturing step of many stages, the bioengineering method needs only a one-stage step in many cases and therefore is expected to simplify the manufacturing step, save costs and shorten the turnaround time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyhydroxyalkanoate-containing structure and manufacturing method thereof
  • Polyhydroxyalkanoate-containing structure and manufacturing method thereof
  • Polyhydroxyalkanoate-containing structure and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

reference example 1

[0131] Preparation of Transformant Capable of Producing PHA Synthesizing Enzyme, And Production of PHA Synthesizing Enzyme

[0132] A transformant capable of producing the PHA synthesizing enzyme was prepared by the following method.

[0133] The YN2 strain was cultured on 100 ml of LB culture medium (1% polypeptone, 0.5% yeast extract, 0.5% sodium chloride, pH 7.4) at 30° C. overnight, followed by isolating and collecting chromosome DNA using a method by Marmer, et al. The obtained chromosome DNA was fully decomposed with a restriction enzyme Hind III. pUC18 was as a vector and cleaved by the restriction enzyme Hind III. Dephosphorylation of the terminal (Molecular Cloning, 1, 572, (1989); Cold Spring Harbor Laboratory Press.) was carried out, and thereafter DNA Ligation Kit Ver. 11 (Takara Shuzo Co., Ltd.) was used to couple the cleaved site (cloning site) of the vector to the Hind III fully decomposed fragment of the chromosome DNA. A plasmid vector with this chromosome DNA fragment ...

reference example 2

Synthesis of 3-hydroxy acyl-CoA

[0153] (R)-3-hydroxy octanoyl-CoA was prepared by the following method, based on Rehm BHA, Kruger N, Steinbuchel A(1998) Journal of Biological Chemistry 273 pp24044-24051, being added with some modification. Acyl-CoA synthetase (manufactured by Sigma-Aldrich Com.) was dissolved in tris-hydrochloric acid buffer solution (50 mM, pH 7.5) containing ATP 2 mM, MgCl2 5 mM, coenzyme A 2 mM, and (R)-3-hydroxyoctanoate 2 mM so as to obtain the resulting solution of 0.1 miliunit / microliter. The solution was incubated in a 37-degree C. of warm bath, and was sampled timely so that progress of a reaction might be analyzed by HPLC. Sulfuric acid was added into a sampled reaction solution to obtain a concentration of 0.02 N to terminate enzyme reaction, and subsequently (R)-3-hydroxyoctanoate that was unreacted substrate was removed by extraction with n-heptane. In analysis by HPLC, RP18 column (nucleosil C18, 7 micrometers, Knauser) was used, elution was conducted ...

example 1

Obtaining of an Amino Acid Sequence Having a Binding Affinity to Copper Phthalocyanine

[0154] (1) Copper phthalocyanine (alpha type: Tokyo Kasei Kogyo Co., Ltd.) was suspended into methanol to obtain a concentration of 5 mg / ml. The suspension 1.5 ml was applied to a plate made of polystyrene, and methanol was removed by evaporation, whereby a coating of copper phthalocyanine was fixed on the surface of the plate made of polystyrene. It was confirmed that the coating of copper phthalocyanine fixed was not removed off even if it was washed with TBS buffer (50 mM Tris-HCl pH7.5 150 mM NaCl) including 0.1% Tween-20.

[0155] (2) A blocking buffer containing bovine serum albumin (BSA) (0.1 M NaHCO3 (pH 8.6), 5 mg / ml BSA, 0.1 mg / ml streptavidin, 0.02% NaN3) was filled on the polystyrene plate with copper phthalocyanine fixed thereon, and kept still standing at 4° C. for one hour. The blocking buffer was then discarded and the plate was washed 10 times by TBST buffer (TBS buffer+0.1% Tween-2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Fractionaaaaaaaaaa
Volumeaaaaaaaaaa
Volumeaaaaaaaaaa
Login to View More

Abstract

A method for manufacturing polyhydroxyalkanoate-containing structure, at least a part of a base material surface of the structure being coated with polyhydroxyalkanoate, the method comprises the steps of immobilizing a polyhydroxyalkanoate synthase on the base material surface, synthesizing, on the base material surface, polyhydroxyalkanoate using a 3-hydroxyacyl coenzyme A to become the substrate of the synthase and the synthase and coating at least a part of the base material surface with the synthesized polyhydroxyalkanoate, wherein the synthase contains an amino acid sequence capable of binding to the base material. A polyhydroxyalkanoate-containing structure, at least a part of a base material surface of the structure being coated with a polyhydroxyalkanoate, comprises the base material, a polyhydroxyalkanoate synthase immobilized on the base material surface, and the polyhydroxyalkanoate with which at least a part of the base material surface is coated, wherein the synthase contains an amino acid sequence capable of binding to the base material.

Description

BACKGROUND OF THE INVENTION [0001] 1. Field of the Invention [0002] The present invention relates to a method for manufacturing polyhydroxyalkanoate-containing structure comprising the steps of immobilizing on a base material polyhydroxyalkanoate synthase involved in polyhydroxyalkanoate biosynthesis reaction and coating at least part of the base material with polyhydroxyalkanoate by polymerizing a 3-hydroxyacyl coenzyme A by use of the enzyme to synthesize the polyhydroxyalkanoate. More particularly, the invention relates to a method for manufacturing polyhydroxyalkanoate-containing structure by immobilizing to a base material polyhydroxyalkanoate synthase containing an amino acid sequence capable of binding to the base material. [0003] The present invention relates to a structure that has polyhydroxyalkanoate, base material and polyhydroxyalkanoate synthase immobilized on the base material, the polyhydroxyalkanoate coating at least part of the base material. The structure of the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B41M5/00C07K7/08G03G9/09C07K17/14C08G63/90C09C3/10C09D11/02C09D11/037C09D11/322C12N9/10C12N11/00C12N15/09C12P7/62G02B5/20G02B5/22G03G9/087
CPCC12N9/1025Y10T428/2989C12P7/625C12N11/00C12P7/62C08G63/90
Inventor NOMOTO, TSUYOSHIYANO, TETSUYAKOZAKI, SHINYAHONMA, TSUTOMU
Owner CANON KK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com