Method for producing wear resistant type plastic floor

A technology of plastic floor and production method, applied in the field of decoration materials, can solve the problems of short service life, low mechanical properties, water resistance, poor wear resistance, etc., and achieve the effects of excellent mechanical properties and excellent weather resistance and corrosion resistance.

Active Publication Date: 2009-02-18
无锡市中德装饰新材料有限公司
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although it has the advantages of lightness and cheap price, it has poor water resistance and wear resistance, low mechanical properties, instability, and it will also warp after watering, poor decorative effect, and short service life, so it is not easy to be accepted by people.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing wear resistant type plastic floor
  • Method for producing wear resistant type plastic floor
  • Method for producing wear resistant type plastic floor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Embodiment 1: The production method of the wear-resistant plastic floor in the embodiment of the present invention adopts the following process steps:

[0039] 1. Mixed and extruded plastic foam floor substrate main and auxiliary materials:

[0040] Firstly, waste plastics (extruded thermosetting plastics PE or PP or PET): such as plastic bottles, plastic basins, etc. are crushed and ground into waste plastic powder with a fineness of 200 meshes, and then spontaneously ignited and dried for use.

[0041] Get waste plastic powder: 35% by weight, add active calcium carbonate (stone powder) to: 55% by weight, plastic reinforcing agent selects chlorinated polyethylene (CPE) as: 2% by weight, plastic filler selects calcium carbonate (stone powder) as: : 3% by weight, calcium stearate is selected as the plastic processing aid: 5% by weight, through high-speed mixing, mixing temperature: 100 ℃, mixing time, 10 minutes, rotating speed: 100 rev / min; Form plastic foam pellets, t...

Embodiment 2

[0047] Embodiment 2: The production method of the wear-resistant plastic floor in the embodiment of the present invention adopts the following process steps:

[0048] 1. Mixed and extruded plastic foam floor substrate main and auxiliary materials:

[0049] Firstly, waste plastics (extruded thermosetting plastics PE or PP or PET) are crushed and ground into waste plastic powder with a fineness of 200 meshes, and then dried naturally for use.

[0050]Get PVC resin powder in the embodiment of the present invention: 45% by weight, add active calcium carbonate (stone powder) to: 45% by weight, plastic reinforcing agent selects methyl methacrylate copolymer as: 3% by weight, plastic filler selects carbonic acid for use Calcium (stone powder) is: 2% by weight, and the plastic processing rib agent is selected from AC foaming agent Azodicarbonamide (DN12) is: 5% by weight, mixed at a high speed, mixing temperature: 110 ° C, mixing time, 13 minutes, Rotational speed: 110 rpm; extruded ...

Embodiment 3

[0056] The production method of the wear-resistant plastic floor of the present invention adopts the following process steps:

[0057] 1. Mixed and extruded plastic foam floor substrate main and auxiliary materials:

[0058] Firstly, waste plastics (extruded thermosetting plastics PE or PP or PET) are crushed and ground into waste plastic powder with a fineness of 200 meshes, and then dried naturally for use.

[0059] In the embodiment of the present invention, the PP plastic raw material is: 55% by weight, adding active calcium carbonate (stone powder) is: 35% by weight, the plastic reinforcing agent is chlorinated polyethylene (CPE): 4% by weight, and the plastic filler is selected from sawdust The fiber powder is: 1% by weight, the foaming regulator (ZB530) is selected as the plastic processing aid: 5% by weight, through high-speed mixing, mixing temperature: 120°C, mixing time, 15 minutes, rotating speed: 120 rpm; Extrude the compounder to extrude into plastic foam pellet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention relates to an abrasion-resistant plastic floor board and its production process. Said process includes the following steps: using waste and old plastic powder as main raw material, adding active calcium carbonate and plastic filling agent as auxiliary raw material, mixing them and extruding them to obtain plastic foamed granules, die-pressing and forming, cooling, setting, drawing and cutting so as to obtain the invented plastic base plate, then sticking plastic protection film on its surface, so that the invented plastic floor board finished product can be made up.

Description

technical field [0001] The invention relates to a production method of a wear-resistant plastic floor, which is used for decoration of family and office rooms, and belongs to the technical field of decoration materials. Background technique [0002] The floor that is used for family, office room decoration usually adopts solid wood floor or compound floor on the market at present. Solid wood flooring consumes a lot of wood and is expensive. Although it has the advantages of wear resistance, it has poor water resistance after laying and use, and is easy to crack and warp. Composite flooring is made by mixing and extruding wood chips and adhesives. Although it has the advantages of lightness and cheap price, it has poor water resistance and wear resistance, low mechanical properties, instability, and it will also warp after being soaked in water. The decorative effect is poor and the service life is short, so it is not easy to be accepted by people. Contents of the inventio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L23/12C08L67/03C08K3/26B29C47/40B29D7/00
Inventor 庄广盛
Owner 无锡市中德装饰新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com