High-strength tooth family alginate impression material
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of dental alginate and impression materials, which is applied in the fields of dental impression materials, dentistry, and compression molding cups, etc., can solve the problems of incompatibility of rigidity and toughness, low strength, etc., and achieve good deformation recovery ability and The effect of compressive strength
Inactive Publication Date: 2009-08-26
QINGDAO BRIGHT MOON SEAWEED GROUP
View PDF3 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0008] The invention provides a dental alginate impression material, which can solve the problems of low strength, rigidity and toughness in the prior art
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0015] High Strength Dental Alginate Impression Material Formula:
[0016] Sodium alginate with M / G value 1.0 14%
[0017] Calcium Sulfate Dihydrate 14%
[0018] Sodium Triphosphate 1.8%
[0019] Diatomaceous earth 69.7%
[0020] Sodium polyacrylate 0.5%
[0021] Mix the above components thoroughly in a mixer to obtain a homogeneous dental alginate impression material.
Embodiment 2
[0023] High Strength Dental Alginate Impression Material Formula:
[0024] Potassium alginate with M / G value of 1.05 13%
[0025] Calcium Sulfate Dihydrate 13%
[0026] Sodium Triphosphate 1.8%
[0027] Diatomaceous earth 71.5%
[0028] Xanthan Gum 0.5%
[0029] Tragacanth Gum 0.2%
[0030] Mix the above components thoroughly in a mixer to obtain a homogeneous dental alginate impression material.
Embodiment 3
[0032] High Strength Dental Alginate Impression Material Formula:
[0033] Sodium alginate with M / G value 1.1 15%
[0034] Calcium Sulfate Hemihydrate 15%
[0035] Sodium pyrophosphate 2%
[0036] Diatomaceous earth 67.5%
[0037] Xanthan Gum 0.3%
[0038] Sodium polyacrylate 0.2%
[0039] Mix the above components thoroughly in a mixer to obtain a homogeneous dental alginate impression material.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a high-strength dental alginate impression material, which is mainly consists of alginate, gelling agent, retarding agent and filling agent. The invention selects the high G alginate with stronger gel rigidity and is further added with one or a plurality of xanthan gum, tragacanth gum and sodium polyacrylate for synergy and a polymer substance is used for improving gel flexibility, so as to prepare the high-strength dental alginate impression material. Compared with the traditional formula products, the high-strength dental alginate impression material of the invention has better deformation recovery ability and pressure resistance intensity, so the invention is more conductive to obtain clear and precise dental impressions.
Description
technical field [0001] The invention belongs to the technical field of new dental materials in stomatology, and in particular relates to a high-strength dental alginate impression material. Background technique [0002] Dental alginate impression material is the basic material for oral restoration to make impression. The main components of alginate impression material are: alginate (such as sodium alginate, potassium alginate, etc.), gelling agent (such as hemihydrate, calcium sulfate dihydrate, etc.), retarders (such as sodium pyrophosphate, sodium carbonate, etc.), fillers (such as pearl salt, kaolin, diatomaceous earth, etc.), the mechanism is: alginate meets Calcium ions later solidify to form a gel: [0003] 2NaAlg+CaSO 4 →Na 2 SO 4 +Ca(Alg) 2 [0004] The above reaction is extremely rapid, which makes the operation difficult. It is necessary to add a retarder in the colloid in advance to adjust the setting time so that it meets the time required for the operation...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more