Xanthation bentonite absorbingsubstance and method for preparing the same

A technology of xanthate and sodium bentonite, which is applied in the preparation of xanthate bentonite, heavy metal ion adsorbent, and xanthate bentonite, can solve the xanthate of bentonite and its application that have not been reported, preparation process and equipment requirements High, time-consuming and labor-intensive application process, etc., to achieve the effects of environmental protection, less dosage, and easy operation

Inactive Publication Date: 2009-11-11
NORTHWEST NORMAL UNIVERSITY
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its raw materials are relatively expensive, the preparation process and equipment requirements are high, the process is relatively complicated, and the application process is time-consuming and labor-intensive, so there are certain defects.
[0005] Various modification methods such as acid activation, salt activation, and organic modification of bentonite and the application of their products have been reported, but there is no report on the xanthification of bentonite and its application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Xanthation bentonite absorbingsubstance and method for preparing the same
  • Xanthation bentonite absorbingsubstance and method for preparing the same
  • Xanthation bentonite absorbingsubstance and method for preparing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Example 1: Add 20g of sodium bentonite to 120mL of distilled water, stir to disperse evenly, add 8g of NaOH, stir at 35°C for 1 hour, add CS dropwise 2 2.41mL, after reacting for 1h, add 5.0g magnesium sulfate and 50mL H 2 O, continue to stir at a constant temperature of 35°C for 30min, filter with suction, wash with 5-10% magnesium sulfate solution for 3-5 times until the filtrate is colorless, and then wash with acetone for 3 times to obtain a light blue-green solid. Vacuum dried for 10 h to obtain product XB1 with a yield of 31.3 g.

Embodiment 2

[0033] Embodiment 2: preparation process and raw material etc. are identical with embodiment 1, and wherein, the add-on of NaOH is 8g, CS 2 The amount of dropping was 7.23mL, and the reaction time was 1h to obtain the XB2 product with a yield of 28.4g.

Embodiment 3

[0034] Embodiment 3: preparation process and raw material etc. are identical with embodiment 1, and wherein, the add-on of NaOH is 8g, CS 2 The amount of the dropwise addition was 7.23mL, and the reaction time was 6h to obtain the XB3 product with a yield of 26.4g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
adsorption capacityaaaaaaaaaa
adsorption capacityaaaaaaaaaa
adsorption capacityaaaaaaaaaa
Login to View More

Abstract

The invention provides a metal ion adsorbent with high adsorption capacity—xanthated bentonite and a preparation method thereof. The high adsorption capacity metal ion adsorbent is prepared by taking sodium bentonite as raw material, reacting with carbon disulfide after dispersion and alkalization, and then transforming with magnesium salt to generate stable magnesium salt of xanthate-based bentonite. The xanthate-based bentonite has strong adsorption capacity for heavy metal ions, and can be applied to the treatment of wastewater containing heavy metal ions. The process of the invention is used for the treatment of heavy metal wastewater, and has the characteristics of simple and easy operation, fast and convenient operation, high removal rate of metal ions, easy separation of solid and liquid, and the like.

Description

technical field [0001] The invention belongs to the technical field of water treatment, and relates to a heavy metal ion adsorbent in the treatment of heavy metal wastewater, in particular to a heavy metal ion adsorbent with high adsorption capacity—xanthated bentonite, and also to a preparation method of xanthated bentonite . Background technique [0002] With the advancement of science and technology and the rapid development of industry and agriculture, people's material living standards continue to improve. However, environmental pollution is also becoming more and more serious. Environmental protection and environmental governance issues are getting more and more attention from the government and all walks of life. An important source of pollution that pollutes the environment and water quality is heavy metal ions in industrial wastewater. Heavy metal wastewater mainly comes from mechanical processing, mining, smelting of steel and non-ferrous metals, and some chemical ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/12B01J20/22C02F1/62
Inventor 王荣民李芳蓉何玉凤李芳莹
Owner NORTHWEST NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products