Method for preparing and rheologic molding semisolid alloy pulp

A semi-solid and alloy technology, applied in the direction of metal processing equipment, etc., can solve the problems of troublesome preparation process and complex structure of the overall equipment, and achieve the effect of reducing preparation cost, energy consumption and difficulty

Inactive Publication Date: 2007-07-25
UNIV OF SCI & TECH BEIJING
View PDF7 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method also requires special mechanical stirring equipment when preparing semi-solid alloy slurry, the composition of the overall equipment is complicated, and the preparation process is cumbersome

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing and rheologic molding semisolid alloy pulp

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] Using a resistance melting furnace to produce ZL101A aluminum alloy (i.e. hypoeutectic Al-7wt% Si-0.45wt% Mg aluminum alloy) liquid with a superheat of 15°C (i.e. the pouring temperature is 630°C), the height of the vertical serpentine runner The diameter is 100mm, the inner diameter is 10mm, the inner arc bend of the serpentine runner is one, and the material of the serpentine runner is graphite. Pour ZL101A aluminum alloy liquid overheated at 15°C directly into the serpentine runner, and flow into the austenitic stainless steel cylindrical preparation crucible along the inner wall of the serpentine runner. When the ZL101A aluminum alloy liquid partially solidifies , the semi-solid ZL101A aluminum alloy slurry can be obtained; the preparation crucible and the semi-solid ZL101A aluminum alloy slurry therein are moved to a temperature controller, which is composed of a 1000Hz intermediate frequency electromagnetic induction coil, and its power is controlled To further co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heightaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

This invention discloses a method for preparing and rheological-molding semi-solid alloy slurry. The method comprises: pouring overheated molten alloy into a crucible through a vertical snake-shaped channel, transferring the crucible with semi-solid alloy slurry into a temperature controller, post-cooling or controlling the temperature field of the semi-solid alloy slurry, pouring the semi-solid alloy slurry into the chamber of an extrusion-casting machine or a press-casting machine, or into the mold of a forging machine, pressing for molding, curing, demolding, and talking out the cast. The method has such advantages as simplified process, lowered energy consumption, shortened process flow, and lowered cost.

Description

technical field [0001] The invention belongs to the technical field of preparation and molding of semi-solid alloy slurry, and particularly provides a preparation and rheological forming method of semi-solid alloy slurry, which is suitable for the preparation and molding of semi-solid alloy slurry. Background technique [0002] Since the invention of semi-solid alloy forming technology by Massachusetts Institute of Technology (MIT) in the early 1970s, the preparation and forming technology of semi-solid alloy slurry has attracted extensive attention and research from all over the world. According to the literature "Behavior of metal alloys in the semisolid state" (M C Flemings, MetallTrans, 1991, 22A: 957-981), "Method and apparatus for shaping semisolid metals" (A Mitsuru, S Hiroto, H Yasunori, et al, EP Patent, 0745694A1, 1996), "A noveltechnique to produce metal slurries for semi-solid metal processing" (J Wannasin, R A Martinez, M C Flemings, [in] Proc of the 9th Int. Co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/00B22D17/00B22D27/04B21J5/02
Inventor 毛卫民杨小容赵振铎汤国兴
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com