Unsaturated monopol polyester foaming plastic and its production

A foamed plastic and castor oil technology, applied in the field of foamed plastics, can solve the problems of large amount of isocyanate, low proportion of natural vegetable oil, lower product cost, etc., and achieves the effect of high cost performance

Inactive Publication Date: 2007-11-21
SUN YAT SEN UNIV
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the hydroxyl group reacts with isocyanate in a molar ratio of 1:1, the amount of isocyanate is relatively large, and the proportion of natural vegetable oil in foamed plastics is not high, which is not conducive to reducing product costs and is not conducive to the biodegradability of foamed plastics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Take 100 parts of castor oil and 26.5 parts of maleic anhydride into a four-necked flask equipped with a thermometer, mechanical stirring and reflux condenser, heat the oil bath to 120°C for 6 hours, and measure the acid value of the reaction system to be 118mgKOH / g. Stop heating, allow reaction product to cool to room temperature naturally, obtain maleic anhydride modified castor oil resin. Its apparent viscosity measured at 30°C is 6850mPa.s.

Embodiment 2

[0035] Take 100 parts of castor oil, 26.5 parts of maleic anhydride, and 0.2 parts of N, N dimethylbenzylamine, add them to a four-neck flask equipped with a thermometer, mechanical stirring and a reflux condenser, heat the oil bath to 90°C for 9 hours, The acid value of the reaction system was measured to be 115 mgKOH / g, the heating was stopped, and the reaction product was naturally cooled to room temperature to obtain a maleic anhydride-modified castor oil resin. Its apparent viscosity measured at 30°C is 4850mPa.s.

Embodiment 3

[0037] Take 100 parts of hydroxyethyl acrylate, 84.5 parts of maleic anhydride, and 0.369 parts of hydroquinone, and put them into a three-necked flask equipped with a thermometer, mechanical stirring and reflux condenser, and heat the oil bath to 90°C for 6 hours. The maleic acid half ester was obtained, and the acid value of the product was 290 mgKOH / g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

A castor unsaturated polyester foaming plastic and production are disclosed. The foaming plastic consists of modified castor resin 100 proportion, vinyl monomer 5-60 proportion, foaming agent 1-15 proportion, foaming stabilizer 0.5-5 proportion, evocating agent 0.5-10 proportion, improver 0-10 proportion, water 0-15 proportion and cross-linking monomer 0-5 proportion. It introduces activated double bond from castor molecular chain. The density of foaming plastic is between 0.1g / cm 3-0.4g / cm 3, compression strength at 25% strain is between 10-900kPa. It's soft and has semi-hard foaming plastic performance and can be used for packing material, furniture materials or shock-reducing foaming material.

Description

technical field [0001] The invention relates to a foamed plastic, in particular to a castor oil unsaturated polyester foamed plastic and a preparation method thereof. technical background [0002] As an important polymer material, foam plastic has been widely used in various fields such as packaging, electrical appliances, furniture, and automobiles. Traditional foam plastics are mostly prepared with petroleum-based products as the main raw materials, which are difficult to degrade under natural conditions and are one of the main causes of white pollution. For this reason, replacing petroleum-based foams with biodegradable foams is a future development trend. In recent years, there have been many studies on the preparation of polymer materials by using vegetable oil instead of some petroleum raw materials. Among them, the method of preparing degradable foam plastics with vegetable oil (such as castor oil and soybean oil, etc.) as the main raw material provides a feasible wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/08C08J9/00C08K5/43C08K5/14C08K3/26
Inventor 容敏智王红娟章明秋