FeZrYB series massive amorphous alloy with excellent soft magnetic property and preparation method thereof

An amorphous alloy and soft magnetic technology, which is applied in the field of FeZrYB bulk amorphous alloy and its preparation, can solve problems such as non-magnetism, and achieve the effect of expanding the application field, overcoming the complex and simple processing technology.

Inactive Publication Date: 2008-02-13
SHANGHAI UNIV
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, Fe-based amorphous alloys with

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • FeZrYB series massive amorphous alloy with excellent soft magnetic property and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1

[0020] The composition (atomic percentage) of the FeZrYB bulk amorphous alloy of this embodiment is: Fe 73%, Zr 2%, Y 4%, and B 21%. The preparation process and steps are as follows: The industrial pure metal raw materials Fe, Zr, Y, and FeB alloy are prepared according to the FeZrYB bulk amorphous alloy composition of this embodiment, and then used in a vacuum non-consumable electric arc furnace under argon protection For smelting, the smelting current density is 150A / cm 2 , The alloy is repeatedly smelted 4 times; a copper mold is used for negative pressure suction casting to obtain a bulk amorphous alloy with a size of 1mm×10mm×80mm. The magnetic properties of the FeZrYB bulk amorphous alloy prepared in this embodiment were measured at room temperature, as shown in FIG. 1. It can be seen from the drawings that the FeZrYB bulk amorphous alloy of the present invention has very excellent magnetic properties, and the saturation magnetization is M s = 1.1T.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a FeZrYB series bulk amorphous alloy with excellent soft magnetic properties and a preparation method thereof. The alloy composition (atomic percentage) of the present invention is: Fe 63-83%, Zr 0.5-6%, Y 2-8%, B 13-27%. The preparation process of the alloy is as follows: the industrial pure metal raw material and FeB are mixed according to the alloy formula, and the vacuum non-consumable electric arc furnace is used for multiple smelting, and the copper mold negative pressure suction casting method is used to cast the bulk amorphous alloy. The bulk amorphous alloy of the invention has excellent soft magnetic properties, and the saturation magnetization is 1.1T. The bulk amorphous alloy of the invention can be widely used in magnetic devices in the fields of information, communication, computer and the like.

Description

technical field [0001] The invention relates to a FeZrYB series bulk amorphous alloy with excellent soft magnetic properties and a preparation method thereof, belonging to the technical field of magnetic alloy materials and processing techniques. Background technique [0002] Amorphous alloys are also called glassy alloys. In 1960, Duwez et al. used the method of rapid cooling of molten metal to obtain Au for the first time. 70 Si 30 Alloy thin strips, thus setting off a research upsurge in the preparation of amorphous materials by rapid cooling. In 1969, Pond invented the single-roll method to prepare amorphous thin strips up to tens of meters, laying the foundation for its industrialization. During the preparation of amorphous alloys, because of the need for very high cooling rates (10 5 K / s or more) make its size very limited, and only very thin or thin strips and filamentous amorphous alloys can be obtained. This limits the practical application of amorphous alloys....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C45/02H01F1/153C22C33/04B22D18/00
Inventor 谭晓华徐晖白琴蒙韬
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap