Light fiberboard and preparation thereof
A technology for lightweight fiberboard and slab, applied in the field of lightweight fiberboard, can solve problems such as environmental pollution, and achieve the effects of reducing product cost, low price and simple preparation process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0033] Example 1
[0034] A kind of lightweight fiberboard whose composition is expressed by mass ratio as:
[0035] 1000kg of poplar (wood) branches, 1kg of polyacrylamide flocculant, 25kg of phenolic resin glue, 1kg of paraffin wax.
[0036] The preparation method includes the following steps:
[0037] (1) Wood selection and slice
[0038] Cut the wood into pieces of 3-10cm in diameter and 1-3cm in length;
[0039] (2) Steaming, hot grinding
[0040] Take the wood section with a moisture content of 30%-50% and place it in a cooking pot for cooking into wood fiber. Make the wood fiber diameter 0.1-0.5mm and length 1-8mm for use. If the wood section moisture content is too high or too low, it should be done first Water content treatment;
[0041] (3) Homogeneous pulping
[0042] Add phenolic resin glue and paraffin wax to the homogenizing tank containing wood fiber, stir for 20-30 minutes, then put the material into the slurry storage well with stirring, and then add polyacrylamid...
Example Embodiment
[0057] Example 2
[0058] A kind of lightweight fiberboard whose composition is expressed by mass ratio as:
[0059] 800kg of mixed branches of poplar, willow and sycamore (wood), 200kg of mixed branches of plow, peach and locust wood, 3kg of polyacrylamide flocculant, 30kg of phenolic resin, 4kg of paraffin wax, 15kg of aluminum sulfate, and commercial brightener VDL2kg, commercial enhancer high-strength cellulose 2kg.
[0060] The preparation method includes the following steps:
[0061] (1) Wood selection and slice
[0062] Cut the wood into pieces of 3-10cm in diameter and 1-3cm in length;
[0063] (2) Steaming, hot grinding
[0064] Take the wood section with a moisture content of 30%-50% and place it in a cooking pot for cooking into wood fiber, making the wood fiber 0.1-0.5mm in diameter and 1-8mm in length for later use;
[0065] (3) Homogeneous pulping
[0066] Add phenolic resin glue, paraffin wax, aluminum sulfate, commercially available brightener VDL, and commercially...
Example Embodiment
[0081] Example 3
[0082] A kind of lightweight fiberboard whose composition is expressed by mass ratio as:
[0083] 700kg of mixed branches of poplar and willow (wood), 300kg of apple wood, 2.5kg of polyacrylamide flocculant, 40kg of phenolic resin, 5kg of paraffin wax, 30kg of aluminum sulfate, 3kg of commercial brightener VDL, commercial enhancer of high-strength cellulose 3kg.
[0084] The preparation method includes the following steps:
[0085] (1) Wood selection and slice
[0086] Cut the wood into pieces of 3-10cm in diameter and 1-3cm in length;
[0087] (2) Steaming, hot grinding
[0088] Take the wood section with a moisture content of 30%-50% and place it in a cooking pot for cooking into wood fiber, making the wood fiber 0.1-0.5mm in diameter and 1-8mm in length for later use;
[0089] (3) Homogeneous pulping
[0090] Add phenolic resin glue, paraffin wax, aluminum sulfate, commercially available brightener VDL, and commercially available enhancer high-strength cellul...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap