PBT/ABS alloy material and preparation method thereof

A technology of alloy materials and compositions, which is applied in the field of PBT/ABS alloy materials and their preparation, can solve the problems of limited wide application, large crystallization shrinkage rate, poor dimensional stability, etc., and achieve excellent physical and mechanical properties, simple preparation process, high The effect of mobility

Inactive Publication Date: 2008-07-09
SHENZHEN KEJU NEW MATERIAL
View PDF0 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its crystal shrinkage rate is large and its dimensional stability is poor.
Although the shrinkage rate can be improved after strengthening, it is

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0041] Example 1:

[0042]The weight ratio of PBT 41%, ABS 12%, compatibilizer 4.4%, enhancer 20% composite flame retardant (decabromodiphenylethane 15%, antimony trioxide 7%), lubricant 0.3%, 1010 0.15 %, 1680.15% are mixed uniformly in a plastic container; put the mixed raw materials into the hopper of the twin-screw extruder, melt and extrude, pelletize, fully plasticize, melt, compound, extrude and stretch , Cooling, pelletizing, drying and packaging; the processing technology is as follows: twin-screw extruder 230°C in the first zone, 235°C in the second zone, 235°C in the third zone, 235°C in the fourth zone, 235°C in the fifth zone, 230°C in the sixth zone, Seven zone 230℃, eight zone 230℃; the screw speed is controlled at 350 rpm; the residence time is 2-10min.

Example Embodiment

[0043] Example 2

[0044] The weight ratio of PBT 26.5%, ABS 26.5%, compatibilizer 6.4%, reinforcing agent 18% composite flame retardant (decabromodiphenylethane 15%, antimony trioxide 7%), lubricant 0.3%, 1010 0.15 %, 168, 0.15%, mixed uniformly in a plastic container; put the mixed raw materials into the feeding hopper of the twin-screw extruder, melt and extrude, pelletize, fully plasticize, melt, compound, and then extrude and draw Strip, cooling, pelletizing, drying and packaging; the processing technology is as follows: twin screw extruder at 230°C in the first zone, 235 in the second zone, 235 in the third zone, 235 in the fourth zone, 235 in the fifth zone, and 230 in the sixth zone. , Seven zone 230 ℃, eight zone 230 ℃; the screw speed is controlled at 350 rpm; the residence time is 2 to 10 min.

Example Embodiment

[0045] Example 3

[0046] The weight ratio of PBT 12.0%, ABS 41%, compatibilizer 3.5%, reinforcing agent 19% composite flame retardant (polybrominated styrene 15%, antimony trioxide 7%), lubricant 0.2%, 1010 0.15% , 1680.15% is mixed uniformly in a plastic container; put the mixed raw materials into the hopper of the twin-screw extruder, melt and extrude, pelletize, fully plasticize, melt, compound, then extrude, stretch, Cooling, pelletizing, drying and packaging; the processing technology is as follows: twin screw extruder at 230°C in the first zone, 235° in the second zone, 235°C in the third zone, 235°C in the fourth zone, 235°C in the fifth zone, 230°C in the sixth zone, and seven Zone 230°C, eight zone 230°C; screw revolutions are controlled at 350 revolutions per minute; residence time is 2-10 min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a PBT/ABS alloy material and a process for preparation, which comprises PBT 10-45%, ABS 10-45%, compatibilizer 1-10%, filling reinforcing agent 10-40%, composite flame retardant 20-30%, lubricating agent 0.1-0.6%, and anti-oxidant 0.1-12%. PBT system and ABS system are welded together through choosing appropriate flame retardant and reinforcing agent, and the invention which is prepared has the character of flame resisting, and which is environment friendly and innocuous, and various physical mechanics properties of the invention are excellent when alloy material is guaranteed to have flame-proof function, and the flame-proof alloy material has the advantages of simple preparation technology, stable sizes, high intensity, aesthetic appearance, high flowability, and drug tolerance and the like.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a PBT / ABS alloy material and a preparation method thereof. Background technique [0002] Polybutylene terephthalate (PBT) is a relatively new type of thermoplastic engineering plastic developed and industrialized by Celanese Corporation of the United States in the 1970s. It has fast crystallization speed, excellent electrical properties and changes with temperature and humidity. Small; good weather resistance, suitable for outdoor use, and excellent chemical resistance; outstanding electrical properties, is an ideal material for electronics and electrical industries, widely used in electronics, electrical, automobiles, household appliances, electric tools, sports equipment, etc. It is also one of the fastest growing engineering plastics in the last decade. However, its crystal shrinkage rate is large and its dimensional stability is poor. Although the shrinkage rate c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/03C08L55/02C08K7/14B29C47/90B29B9/12C08K3/00C08K5/06C08K5/524B29C48/90
Inventor 徐东贺永李茂林
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka