Fluorocarbon compound modified polyacrylate flow agent for coating ink and production method thereof

A technology of fluorocarbons and polyacrylates, applied in the direction of coating, etc., can solve the problems of unsatisfactory working effect, complicated production process, and complicated raw materials, and achieve the effects of low production cost, increased surface gloss, and simple production methods

Active Publication Date: 2008-07-23
ANHUI XOANONS CHEM
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing leveling agent for paint and ink has complex raw materials, high cost, complex production process and unsatisfactory working effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) Xylene 1-10% (example 1%, 5%, 10%), toluene 1-10% (example 1%, 5%, 10%), propylene glycol methyl ether 1-20% (example 1%) , 19%, 20%) into the reactor, heated to 80 ~ 120 ℃ (for example 80 ℃, 100 ℃, 120 ℃);

[0022] (2) Add 30% to 70% of acrylate monomer (example 30%, 50%, 70%), initiator peroxide diphenyl ether (or azobisisobutyronitrile) 1% to 10% (example 1 %, 5%, 10%), acrylic acid fluorine monomer 1-20% (example 1%, 10%, 20%) at 80-150°C (example 80°C, 110°C, 150°C), 3- Put it into the above reaction kettle within 5 hours, keep it warm at 80-150°C (eg 80°C, 110°C, 150°C) for 2-5 hours to obtain the product.

[0023] The above-mentioned usage percentages are percentages by weight.

[0024] Wherein the acrylate monomer is methyl methacrylate (or butyl acrylate, etc.). The fluorine acrylate monomer is perfluoroalkyl acrylate (or nonadecafluoroheptyl acrylate, dodecafluoroheptyl methacrylate, hexafluorobutyl acrylate, etc.).

Embodiment 2

[0026] (1) Put xylene, toluene, and propylene glycol methyl ether into the reaction kettle, and heat up to 80-120°C (for example, 80°C, 100°C, 120°C);

[0027] (2) Add 30% to 70% of acrylate monomer (for example, 30%, 50%, 70%), initiator peroxydiphenyl ether (or azobisisobutyronitrile), acrylate fluorine monomer 1~20% (example 1%, 10%, 20%) at 80~150 ℃ (example 80 ℃, 110 ℃, 150 ℃), add in the above-mentioned reactor within 3~5 hours, 80~150 ℃ (example 80°C, 110°C, 150°C) for 2 to 5 hours to obtain the product.

[0028] Then add xylene to 1-10% (example 1%, 5%, 10%), toluene to 1-10% (example 1%, 5%, 10%), propylene glycol methyl ether to 1-20% ( Example 1%, 19%, 20%) and initiator diphenyl ether peroxide (or azobisisobutyronitrile) to 1-10% (example 1%, 5%, 10%), at 80-150°C Keep warm for 2-5 hours.

[0029] The above-mentioned usage percentages are percentages by weight.

[0030] Wherein the acrylate monomer is methyl methacrylate (or butyl acrylate, etc.). The fluorine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fluorocarbon modified polyacrylate flow agent used for paint and ink and the production method, which is manufactured by the reaction of acrylate monomer, initiator, acrylic fluoride monomer, xylene, toluene and propylene glycol methyl ether. The fluorocarbon modified polyacrylate flow agent has the advantages of easily available materials, low production cost, simple preparation method, convenient use and increased surface glass of paint and ink.

Description

Technical field: [0001] The invention relates to a leveling agent for coating ink and a production method. Background technique: [0002] The existing leveling agent for paint and ink has complex raw materials, high cost, complex production process and unsatisfactory working effect. Invention content: [0003] The object of the present invention is to provide a fluorocarbon modified polyacrylate leveling agent for paint and ink with easy-to-obtain raw materials, low production cost and simple production method and a production method. [0004] Technical solution of the present invention is: [0005] A kind of fluorocarbon compound modified polyacrylate leveling agent for coating ink is characterized in that: it is made by the raw material reaction of following percentage by weight: [0006] Acrylate monomer 30~70% [0007] Initiator 1~10% [0008] Acrylic acid fluorine monomer 1~20% [0009] Xylene 1~10% [0010] Toluene 1~10% [0011] Propylene glycol methyl ether ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D7/06C08F220/10C08F8/18C09D7/47
Inventor 陈永康
Owner ANHUI XOANONS CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com