A kind of preparation method of bisphenol A bis(diphenyl phosphate)

A technology of diphenyl phosphate and phenol, applied in the field of preparation of bisphenol A bisphenol A, can solve the problems of unstable purity of the target product, not easy to react completely, and impact on the production environment, achieve good economic and social benefits, and avoid corrosion , the effect of reducing labor intensity

Active Publication Date: 2012-02-22
山东旭锐新材股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These methods all are to adopt the mode of solid bisphenol A to add material to carry out, difficult reaction is complete; Reaction is carried out under non-vacuum state, because the influence of air easily produces impurity, makes the purity of target product unstable; The HCl gas that produces in the production process Generate acid and corrode equipment, and have a great impact on the production environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of bisphenol A bis(diphenyl phosphate)

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment 1, 80g (0.351mol) bisphenol A and 245g (1.596mol) phosphorus oxychloride are added to the four ports of dry, replaced with nitrogen and equipped with stirrer, thermometer, nitrogen inlet pipe, oil heating device In the flask, raise the temperature to 60°C and stir slowly until the bisphenol A is completely dissolved, as the dissolved material, keep warm for later use; weigh 1.5g of anhydrous aluminum trichloride and 100g (0.651mol) of phosphorus oxychloride In a four-necked flask equipped with a stirrer, reflux pipe, thermometer, nitrogen gas introduction pipe, heating device and hydrogen chloride absorption device, the temperature was raised rapidly to 90 °C, and then the above dissolved materials were slowly added dropwise, and added dropwise over 3 hours. Completed, then reacted for 2 hours under the condition of gradient temperature increase from 110°C to 130°C, then cooled the material to below 60°C under the condition of feeding a small amount of nitroge...

Embodiment 2

[0019] Embodiment 2, 80g (0.351mol) bisphenol A and 230g (1.503mol) phosphorus oxychloride are made into dissolved material; Weigh 1g anhydrous aluminum trichloride and 90g (0.586mol) phosphorus oxychloride in four ports Rapidly heat up to 70°C in the flask, then add the above-mentioned dissolved materials dropwise in the time of 2 hours, distill out excessive phosphorus oxychloride after the completion of the reaction, add 127g (1.351mol) phenol in the material that has been distilled. React for 8 hours under the condition of gradient temperature rise from 70°C to 150°C, and finally wash to obtain the target product. Other technical characteristics are the same as embodiment 1.

Embodiment 3

[0020] Embodiment 3, 80g (0.351mol) bisphenol A and 280g (1.824mol) phosphorus oxychloride are made into dissolved material; Weigh 2g anhydrous aluminum chloride and 150g (0.977mol) phosphorus oxychloride in four ports Rapidly heat up to 80°C in the flask, then add the above-mentioned dissolved materials dropwise in the time of 2 hours, distill out excessive phosphorus oxychloride after the completion of the reaction, add 136g (1.446mol) phenol in the material that has been distilled. React for 10 hours under the condition of gradient temperature rise from 70°C to 150°C, and finally wash to obtain the target product. Other technical characteristics are the same as embodiment 1.

[0021] It is found through testing that the product prepared by using the preparation method of the present invention has stable quality and superior performance, and its normalized area is 4% higher than that of the product prepared by the existing method on average. The following table is the HPLC ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
Login to View More

Abstract

A method for preparing bisphenol A bis(diphenyl phosphate), which is characterized by adding a certain amount of bisphenol A and phosphorus oxychloride into a reactor, heating and stirring until all bisphenol A is dissolved, and the method is Obtain dissolved materials; add a certain amount of Lewis acid and phosphorus oxychloride into the reactor with a hydrogen chloride absorption device, rapidly heat up, add the above dissolved materials dropwise, after the reaction is completed, distill out excess phosphorus oxychloride, and then Add a certain amount of phenol, adjust the temperature until the reaction is completed, and obtain the target product after washing and removal of benzene. The products produced by the preparation process of the present invention are of good quality, can reduce labor intensity, improve the working environment, and have good economic and social benefits.

Description

Technical field [0001] The invention belongs to a preparation method of bisphenol A bis(diphenyl phosphate). Background technique [0002] Bisphenol A bis(diphenyl phosphate) belongs to a new generation of condensed non-halogenated organophosphorus flame retardants. It has excellent thermal stability and low volatility, and is widely used in flame retardant PVC, cellulose resin, synthetic Rubber, phenolic resin, epoxy resin, polyester fiber, etc. are also flame retardants and extreme pressure wear-resistant agents for lubricating oil esters. At present, there are three main synthetic methods of bisphenol A bis(diphenyl phosphate): one is to react bisphenol A with phosphorus oxychloride to obtain bisphenol A (bis-dichlorophosphate), and then use phenol to block , Obtain target product; The 2nd, obtain diphenylphosphoryl chloride with phenol reaction earlier with phosphorus oxychloride, then obtain target product with bisphenol A reaction; Dichlorophosphate) to obtain the ta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07F9/32C09K21/12
Inventor 杨树仁郝建港王志强张荣华段俊彪于文智王洪刚
Owner 山东旭锐新材股份有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com