Low grade tailing steel slag re-use method and slurry magnetic separation equipment
A low-grade, steel slag technology, applied in clay processing equipment, chemical instruments and methods, magnetic separation, etc., can solve problems such as waste of resources, environment, pollution, etc., and achieve outstanding economic and social benefits.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0030] Example 1
[0031] Sieving low-grade (total iron content 18%) and small particle size (below 10mm) steel slag. While sieving, 5-10mm steel slag particles are subjected to dry magnetic separation, and 5-10mm steel slag particles are scrap iron. The recovery rate is 18%. The recycled scrap iron (40% total iron content) is metallurgically reused. Steel slag particles with a total iron content below 10% are used as coarse aggregates for standard bricks and porous bricks.
[0032] The steel slag below 5mm and the water are in a weight ratio of 1:0.6, and two thousandths of the total weight of the water reducing and grinding aid are mixed and added to the wet ball mill for ball milling. After ball milling until the slurry fineness reaches 0.08mm square hole sieve and the sieve is less than 15%, the iron can be separated from the grinding, and the steel slag slurry is discharged into the double-bin magnetic separator for iron separation. The iron powder recovery rate after cleanin...
Example Embodiment
[0037] Example 2
[0038] Sieving low-grade (total iron content 20%) and small particle size (below 10mm) steel slag. While sieving, 5-10mm steel slag particles are subjected to dry magnetic separation for iron separation, and 5-10mm steel slag particles are scrap iron. The recovery rate is 19.5%. The recovered scrap iron (42% total iron content) is metallurgically reused. Steel slag particles with a total iron content below 10% are used as coarse aggregates for standard bricks and porous bricks.
[0039] The steel slag below 5mm and water are in a weight ratio of 1:0.6, plus two thousandths of the total weight of water reducing and grinding aids are mixed into the wet ball mill for ball milling, ball milling until the slurry fineness reaches 0.08mm square hole sieve sieve Less than 15% can be used for grinding iron, and the steel slag slurry is discharged into the double-bin magnetic separator for iron separation. The iron powder recovery rate after cleaning is 13%, the total iro...
Example Embodiment
[0044] Example 3
[0045] Sieving low-grade (total iron content 16%) and small particle size (below 10mm) steel slag. While sieving, 5-10mm steel slag particles are subjected to dry magnetic separation, and 5-10mm steel slag particles are scrap iron. The recovery rate is 17%. The recovered scrap iron (total iron content of 38%) is metallurgically reused, and steel slag particles with a total iron content of less than 10% are used as coarse aggregates for the production of standard bricks and porous bricks.
[0046] The steel slag below 5mm and water are in a weight ratio of 1:0.6, plus two thousandths of the total weight of water reducing and grinding aids are mixed into the wet ball mill for ball milling, ball milling until the slurry fineness reaches 0.08mm square hole sieve sieve Less than 15% can be used for grinding iron, and the steel slag slurry is discharged into the double-bin magnetic separator for iron separation. The iron powder recovery rate after cleaning is 10%, the...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap