Dyeing and finishing process of polyolefin elastic fiber fabric coated by polyester cotton filling yarn

A technology of warp and weft yarns and elastic fibers, which is applied in the processing technology field of elastic fabrics, and can solve problems such as unstable width, decreased elasticity, unreasonable process parameters and process flow, etc.

Inactive Publication Date: 2009-03-25
HUAFANG
View PDF0 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing polyester-cotton warp and weft yarn-wrapped polyolefin elastic fiber fabric dyeing and finishing process, due to the unreasonable selection of treatment liquid raw materials, process parameters, and process flow, causes the strength of the fabric to decrease, the elasticity to decrease, and the width to be unstable. And other issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] In the polyester-cotton warp and weft yarn-wrapped polyolefin elastic fiber fabric, the polyolefin elastic fiber is DOW XLA polyolefin elastic fiber, produced by Dow Chemical Company, the thickness of the fiber is 40D (Denier, Denire), and the tissue specification: polyester cotton CVC40+40D(XLA)X40+40D(XLA) 96X72 79".

[0025] The dyeing and finishing process adopted has the following steps in sequence,

[0026] a. Turn over the seam, the front and back are the same, the seam head is straight and firm, the edges on both sides are dense, and the stitch density is 28 stitches / 10cm;

[0027] b, Narrowing, first rolling material, the components of the rolling material are: 301L refining enzyme 10g / L, oxalic acid 1g / L, penetrant CWA 3g / L, the rest is water, the temperature of the rolling material is 55°C, after rolling the material is Stack in the crawler box at 60°C for 35 minutes, then wash with 80°C hot water in a 5-grid washing tank, and the width shrinks by 18%;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a dyeing and finishing technology for using polyester cotton warp and weft yarn to warp a polyolefin elastic fiber fabric, and belongs to a processing technology of an elastic fabric. The technology sequentially includes the following steps: turning and sewing of the cloth, shrinking, singeing, desizing, mercerizing, setting, dyeing, after finishing and pre-shrinkage. The dyeing and finishing technology decreases the density of the warp and weft direction during the preliminary treatment before the dyeing of the fabric, and leads the cloth easier to retract, and the width is sufficiently shrunk after the shrinkage, desizing and mercerization process, thus obtaining the cloth has good elastic effect and soft feeling. Compared with the prior art, the fabric has good tensile recovery property, stable and lower washing shrinkage and high temperature resistance, strong acid resistance and strong alkaline resistance, which is favorable for various professional finishing; therefore, the soft dacron-cotton warp and weft elastic fabric with high elasticity, good air permeability and strong moisture absorption property can be obtained.

Description

technical field [0001] The invention relates to a processing technology of an elastic fabric, in particular to a pre-treatment and post-finishing process of a polyester-cotton warp and weft yarn-wrapped polyolefin elastic fiber fabric. Background technique [0002] At present, elastic fabrics on the market are generally made of spandex, nylon and polyester interwoven. This kind of fabric is easy to shrink and melt when heated (high temperature), making it difficult to burn singeing. It is difficult to ensure the width, elastic elongation and rebound of the finished product when shaping. rate and weft shrinkage, and will be attacked by alkali and available chlorine, which will cause the elastic fibers to break bonds and hydrolyze, resulting in a decrease in elasticity and strength. And it is not resistant to high temperature finishing, such as anti-wrinkle finishing, waterproof and oil-proof finishing, and has poor dimensional stability. However, DOWXLA polyolefin elastic fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06C27/00D06C9/00D06C7/02D06M16/00D06L1/14D06B7/00D06P1/16
Inventor 王力民李付杰李春光李玉华王旭州刘成林韩丽程云
Owner HUAFANG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap