Imitating metal fluorocarbon coatings using aluminium powder slurry after surface treatment

A technology of surface treatment and aluminum powder paste, applied in the direction of inorganic pigment treatment, chemical instruments and methods, fibrous fillers, etc., can solve the problem that aluminum powder or aluminum paste is easily corroded, the decorative effect is destroyed, and the application of imitation metal fluorocarbon paint is affected and other problems, to achieve the effect of good long-lasting color retention, strong apparent metallic texture, and excellent discoloration

Inactive Publication Date: 2009-04-01
SKSHU PAINT
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the application of wall construction, the general imitation metal fluorocarbon paint is made of ordinary aluminum powder paste. Under the action of alkalinity on the wall, the aluminum powder or aluminum paste is easily eroded, and the decorative effect is caused by falling powder and blackening. Destruction, affecting the application of imitation metal fluorocarbon paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] The preparation method of this imitation metal fluorocarbon paint:

[0044] 45-55 parts of hydrocarbon-containing fluorocarbon resin, 5-10 parts of aluminum powder or aluminum paste coated with polymer or inorganic matter, 10-25 parts of aluminum powder alignment aid, and 0.1-0.3 parts of Add the wetting and dispersing agent into the container, disperse and stir evenly at a low speed, the stirring speed is 0-500 rpm, preferably 200 rpm, and then add 0.1-0.8 parts of anti-settling agent and 10-30 parts of solvent to adjust the viscosity to pass.

[0045] Then, according to the ratio of 16 to 19:1, mix component 1 and component 2 evenly to form the imitation metal fluorocarbon paint.

[0046] The amounts and parts of the above-mentioned raw materials all refer to the weight ratio.

[0047] The performance measurement of the imitation metal fluorocarbon paint produced according to the above ratio and process is shown in the following table 1:

[0048] Table 1 Performanc...

Embodiment 1

[0052] Component one:

[0053] Component Weight ratio

[0054] 1. Hydroxy-containing fluorocarbon resin 45

[0055] 2. Polymer coated aluminum powder 12

[0056] 3. Wetting and dispersing agent 0.1

[0057] 4. 20% cellulose acetate butyrate 25

[0058] 5. Anti-settling agent 0.1

[0059] 6. Butyl acetate 17.8

[0060] Component two:

[0061] Hexamethylene diisocyanate trimer.

[0062] Above-mentioned component one and component two proportion by weight are as follows:

[0063] Component one: component two = 16:1.

[0064] The preparation method of this imitation metal fluorocarbon paint:

[0065]Add the above hydrocarbon-containing fluorocarbon resin, polymer-coated aluminum powder, 20% cellulose acetate butyrate, and wetting and dispersing agent into the container, disperse and stir at 100 rpm, and then add anti-settling agent, butyl acetate Adjust viscosity with ester to pass.

[0066] Then according to the ratio of 16:1, mix component 1 and component 2 evenly to ...

Embodiment 2

[0068] Component one:

[0069] Component Weight ratio

[0070] 1. Hydroxy-containing fluorocarbon resin 54

[0071] 2. Polymer coated aluminum paste 11.5

[0072] 3. Wetting and dispersing agent 0.2

[0073] 4. 20% cellulose acetate butyrate 24

[0074] 5. Anti-settling agent 0.3

[0075] 6. Xylene 10

[0076] Component two:

[0077] Hexamethylene diisocyanate trimer.

[0078] Above-mentioned component one and component two proportion by weight are as follows:

[0079] Component one: component two = 19:1.

[0080] The preparation method of this imitation metal fluorocarbon paint:

[0081] Add the above-mentioned hydrocarbon-based fluorocarbon resin, polymer-coated aluminum powder, 20% cellulose acetate butyrate, and wetting and dispersing agent into the container, disperse and stir at 150 rpm, and then add anti-settling agent, butyl acetate Adjust viscosity with ester to pass.

[0082] Then, according to the ratio of 19:1, mix component 1 and component 2 evenly to f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A pseudo-metallic fluorocarbon paint adopts polymer or inorganic substance-coated aluminum paste, solving the problems of darkening and peeling caused by insufficiency of alkali resistance of untreated aluminum powder paste used in the prior art. The pseudo-metallic fluorocarbon paint comprises composition I including hydroxyl fluorocarbon resin, the polymer or inorganic substance-coated aluminum paste, wetting and dispersing agent, cellulose acetate butyrate, anti-settling sagging agent and solvent; and composition II, hexamethylene diisocyanate (HDI) trimer, wherein, the proportion of composition I to composition II is 16-19:1. The pseudo-metallic fluorocarbon paint prepared by using such compositions including polymer or inorganic substance-coated aluminum paste, in such a proportion, has the advantages of extraordinary alkali and color-changing resistance, so in alkaline environment, aluminum powder erosion changes seldom occur. When being applied to building walls for coating protection, the paint has excellent color retention performance.

Description

【Technical field】 [0001] The invention relates to a paint, in particular to a surface-treated aluminum powder paste imitation metal fluorocarbon paint. 【Background technique】 [0002] In the decoration of the exterior wall of high-rise buildings, there is an imitation metal fluorocarbon paint cured at room temperature, which can meet the conditions of room temperature environment, and through the construction process, it can complete the decoration and protection effect of the hanging panel similar to the aluminum-plastic panel curtain wall, and has excellent weather resistance. , Such as resistance to ultraviolet radiation, wind erosion, chalking resistance to atmospheric corrosion. However, in the application of wall construction, the general imitation metal fluorocarbon paint uses ordinary aluminum powder paste. Under the action of alkalinity on the wall, the aluminum powder or aluminum paste is easily eroded, and the powder and blackening cause decorative effects. Destr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/12C09D7/12C09C3/00
Inventor 洪杰张喜强
Owner SKSHU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap