Method for producing 3004 grade aluminium alloy material used for Venetian blind

A manufacturing method, aluminum alloy technology, applied in the direction of metal rolling, etc., can solve the problems of high equipment investment cost, low yield rate, high cost, etc., and achieve the effect of simple manufacturing process, low cost and short production cycle

Inactive Publication Date: 2009-05-20
JIANGSU ALCHA ALUMINUM CO LTD
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, 3004 aluminum alloy materials for shutters are mainly produced by hot rolling-cold rolling. Although the product quality is good, the process is long, the cost is high, the yield rate is low, and the equipment investment cost is high. The product price is significantly higher than that of ordinary aluminum alloys of the same type. Sheet and Strip Products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 1) Casting and rolling of slabs: industrial pure aluminum ingots for remelting, aluminum-iron master alloy ingots, aluminum-silicon master alloy ingots, aluminum-copper master alloy ingots, aluminum-manganese master alloy ingots, The magnesium ingots and zinc ingots are added into the smelting furnace to be melted and heated to 700°C. After refining, slag removal, stirring, analysis and adjustment of components, they enter the stationary furnace, where the stationary furnace is subjected to stationary, refining, degassing and slag removal. ; In order to improve the microstructure of the aluminum plate and the distribution and structure of the second phase particles, after the aluminum liquid is led out of the static furnace, the aluminum-titanium-boron wire refiner adding device is activated in the flow tank and the mass percentage of 0.015 is added to the aluminum liquid. % titanium element; then it is degassed and filtered outside the furnace, and then enters the casti...

Embodiment 2

[0027] 1) Casting and rolling of slabs: industrial pure aluminum ingots for remelting, aluminum-iron master alloy ingots, aluminum-silicon master alloy ingots, aluminum-copper master alloy ingots, aluminum-manganese master alloy ingots, The magnesium ingots and zinc ingots are added into the smelting furnace to be melted and heated to 710°C. After refining, slag removal, stirring, analysis and adjustment of components, they enter the stationary furnace, where the stationary furnace is placed, refined, degassed, and slag removed. ; In order to improve the microstructure of the aluminum plate and the distribution and structure of the second phase particles, after the aluminum liquid is led out of the static furnace, the aluminum-titanium-boron wire refiner adding device is activated in the launder and the mass percentage of 0.020 is added to the aluminum liquid. % titanium element; then it is degassed and filtered outside the furnace, and then enters the casting and rolling unit ...

Embodiment 3

[0034] 1) Casting and rolling of slabs: industrial pure aluminum ingots for remelting, aluminum-iron master alloy ingots, aluminum-silicon master alloy ingots, aluminum-copper master alloy ingots, aluminum-manganese master alloy ingots, The magnesium ingots and zinc ingots are added into the smelting furnace to be melted and heated to 730°C. After refining, slag removal, stirring, analysis and adjustment of components, they enter the stationary furnace, where they are left to stand, refine, degas, and remove slag. ; In order to improve the microstructure of the aluminum plate and the distribution and structure of the second phase particles, after the aluminum liquid is led out of the static furnace, the aluminum-titanium-boron wire refiner adding device is activated in the launder and the mass percentage of 0.018 is added to the aluminum liquid. % titanium element; then it is degassed and filtered outside the furnace, and then enters the casting and rolling unit for casting and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for manufacturing a No. 3004 aluminum alloy material used for a shutter, which maintains good surface quality of an aluminum strip, fine grain structure, leveled profile shape of a finished product, uniform thickness and high dimension precision through optimized casting, cold rolling and intermediate annealing. Moreover, the forming property and the camber stability accord with the requirements of the shutter product, and simultaneously the method has simple manufacturing technique, short production period, low cost and obvious productivity effect, and can use a cast and rolled plate blank to produce the aluminum material with good mechanical property, profile shape and surface quality for the shutter to meet the user requirements.

Description

technical field [0001] The invention relates to a manufacturing method of an aluminum alloy material, in particular to a manufacturing method of a 3004-grade aluminum alloy material for shutters. Background technique [0002] Aluminum alloy shutters are favored by the market due to their high hardness, beautiful appearance and durability, and the market demand is increasing. [0003] At present, the 3004 grade aluminum alloy materials for shutters are mainly produced by the hot rolling-cold rolling method. Although the product quality is good, the process is long, the cost is high, the yield is low, and the equipment investment cost is high. The product price is significantly higher than that of ordinary aluminum alloys of the same type. Strip products. SUMMARY OF THE INVENTION [0004] Aiming at the above defects, the present invention provides a method for manufacturing 3004 grade aluminum alloy material for blinds, through optimized casting, cold rolling and intermedia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23P17/00C22C1/03B21B1/46C22F1/04
Inventor 章建华何献忠张建军张月华
Owner JIANGSU ALCHA ALUMINUM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com