Anti-corrosive powder paint for steel support frame

A powder coating and support frame technology, applied in powder coatings, anti-corrosion coatings, polyester coatings, etc., can solve the problems of long product cycle, low labor production efficiency, health hazards, etc., to improve labor production efficiency, The effect of saving labor and production cost and avoiding fire

Inactive Publication Date: 2009-05-20
扬州三川实业有限公司
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Furthermore, if you use a drying-type solvent-based coating, although the coating performance is better than that of the self-drying type, it cannot avoid the problem of multiple coating and drying, and it also needs to go through coating-baking. —coating—baking—painting—baking process, for a coating film thickness of 70-80 microns, that is, three times of coating and three times of baking are required to achieve the required coating thickness
Because of the many times of painting and baking, the production cycle is long and the labor production efficiency is not high
If solvent-based coatings are used, a large amount of organic solvents (almost 50% are volatile organic solvents) will be volatilized during the production process, which will not only waste a large amount of organic solvents, but also cause air pollution and unsafe factors that are likely to cause fires. cause certain harm to human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Formula example of electrostatic coating epoxy powder coating for anti-corrosion of mine steel support frame: 56 parts of epoxy resin or phenolic modified epoxy resin, 14 parts of phenolic hydroxyl resin, 25 parts of pigment and filler, 1.0 part of leveling agent, 0.5 parts of accelerator parts, 0.5 parts of degassing agent, and 3.0 parts of other additives. The curing condition of this powder coating is 180°C / 6min.

Embodiment 2

[0021]Formula example of polyester epoxy powder coating for anti-corrosion special electrostatic coating of mine steel support frame: 35 parts of carboxyl-terminated epoxy resin, 35 parts of bisphenol A epoxy resin, 25 parts of pigment and filler, 1.0 part of leveling agent, degassing 0.5 parts of additives, 3.5 parts of other additives. The curing condition of this powder coating is 180°C / 6-8min (or 140°C for 20min).

Embodiment 3

[0023] Formula example of polyurethane powder coating for anti-corrosion special electrostatic coating of mine steel support frame: 56 parts of hydroxyl-terminated polyester resin, 14 parts of blocked polyisocyanate curing agent, 25 parts of pigment and filler, 1.0 part of leveling agent, and 0.5 part of degassing agent , Other additives 3.5 powder. The curing condition of this powder coating is 180°C / 20min.

[0024] The film performance of this powder coating can reach the following indicators: the appearance of the film is smooth with slight orange streaks, the gloss reaches a gloss value of more than 80, the impact strength is 50 cm, the pencil hardness reaches H or above, and the adhesion (cross-cut method) is 0~ Level 1, the bending test reaches 3mm, and the cupping test reaches 6mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention relates to an anticorrosive powder coating used for steel supporting frames, belonging to the technical field of powder coating; the coating is mainly characterized in that: according to the mass percentage, the anticorrosive powder coating comprises 35-58 percent of thermosetting resin, 4.5-35 percent of curing agent, 20-35 percent of pigment and filling material and 2-5 percent of auxiliary agent. The anticorrosive powder coating can avoid the environmental pollution and the damage on health of people caused by the use of solvent based coating, also can save the limited resource organic solvent, improves the effective utilization ratio of the coating, improves the labor productivity, can achieve the required coating thickness and the anticorrosive performance by one-time coating, saves the labor production cost, has good safety performance during the production and avoids the unsafe factors such as fire, and the like caused by the use of the organic solvent.

Description

technical field [0001] The invention relates to an anticorrosion powder coating for a steel support frame, which belongs to the technical field of powder coatings. Background technique [0002] With the improvement of mine automation production technology and the strict requirements of safety production, a large number of support frames are used in the support of mine tunnels. At present, such support frames generally use logs. With the reduction of forest resources, a large number of logs are used to support the tunnel, which brings certain difficulties. In various mining industries, a large number of steel support frames have been used to support the tunnels, gradually replacing the wood used in large quantities in the past, to ensure the safety of the mine tunnels and normal mining work. Due to the complex natural environment of the mine, the composition of various gases, liquids and solid dust volatilized in the mining area is very complex, and the corrosion of the stee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D167/00C09D175/04C09D5/03C09D5/08
Inventor 薛志荣杨军政
Owner 扬州三川实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products