Fully biodegradable polyhydroxyalkanoate/polybutylene succinate blend gold
A technology of polybutylene succinate and polyhydroxyalkanoate, which is applied in the field of materials, can solve the problems of accelerated crystallization nucleation, complex reaction products, high melting temperature, etc., and achieve good processability, accelerated degradation rate, The effect of expanding the range of application
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] The fully biodegradable polyhydroxyalkanoate / polybutylene succinate blend alloy of the present embodiment, by weight, has the following components: PHB content 55%, PBS 30%, cornstarch 8%, Talc powder 5%, polyethylene wax 0.75%, calcium stearate 0.5%, aluminate coupling agent 0.15%, boron nitride 0.3%, tetrakis [β-(3,5-di-tert-butyl-4-hydroxy 0.2% of pentaerythritol phenyl) propionate and 0.1% of tris(2,4-di-tert-butylphenyl) phosphite.
Embodiment 2
[0026] The fully biodegradable polyhydroxyalkanoate / polybutylene succinate blend alloy of the present embodiment, by weight, the contents of each component are: P3HB4HB (4HB molar content is 5%) content of 45%, PBS 35%, tapioca starch 10%, calcium carbonate 8%, EBS 0.5%, zinc stearate 0.5%, titanate coupling agent 0.2%, silicon dioxide 0.5%, tetrakis [β-(3,5-di tert-butyl-4-hydroxyphenyl)propionate]pentaerythritol 0.2%, tris(2,4-di-tert-butylphenyl)phosphite 0.1%.
Embodiment 3
[0028] The fully biodegradable polyhydroxyalkanoate / polybutylene succinate blend alloy of the present embodiment, by weight, each component content is respectively: PHBV (HV molar content is 7%) content 30%, PBS45%, potato starch 18%, montmorillonite 5%, TAF0.5%, barium stearate 0.5%, titanate, aluminate composite coupling agent 0.1%, lanthanum benzoate 0.6%, 2-tertbutyl 0.2% of 6-(3-tert-butyl-2-hydroxy-5-methylbenzyl)-4-methylphenyl acrylate and 0.1% of tris(2,4-di-tert-butylphenyl)phosphite.
PUM
Property | Measurement | Unit |
---|---|---|
glass transition temperature | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
tensile yield strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com