Aqueous low smoke low toxicity fire-resisting paint for thin section steel structure and preparation thereof
A fire-resistant coating, water-based technology, applied in the field of coatings, can solve the problems of fire personnel and firefighters' injuries, environmental pollution, etc., and achieve the effects of short drying time, high bonding strength and excellent water resistance
Active Publication Date: 2011-06-01
应急管理部四川消防研究所
View PDF0 Cites 3 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0009] Therefore, the combustion products of thin steel structure fire retardant coatings are a serious injury to those who have not escaped from the fire scene and firefighters, and will cause great environmental pollution at the same time.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0047] The components in parts by weight of the water-based low-smoke and low-toxic thin steel structure fireproof coating of the present invention are shown in Table 3.
[0048] Table 3 embodiment material ratio table
[0049]
Example 1
Example 2
Example 3
Example 4
Example 5
Water Soluble Acrylate Emulsion
35
31
39
18
42
Low sulfur expandable graphite
3
14
11
16
17
7
10
6
4
18
20
9
5
4
6
Spherical closed cell expanded perlite
6
3
5
2
4
filler
3
4
5
8
7
0.4
0.1
0
0.5
-
Anti-settling agent
0.5
0
0.9
1.5
-
[0050]The preparation methods of each embodiment are the same, that is, according to the consumption in Table 3, ammonium polyphosphate, wolla...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| particle diameter | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to a water-based low smoke low toxicity thin type fire resisting coating for a steel structure and a preparation method thereof, which belongs to technical field of coating. The invention aims to improve the main performance indexes of the prior thin type fire resisting coating for the steel structure such as fire resisting performance, bond strength, water resistance, cold and hot cycle resistance, and the like, and reducing the quantity and toxicity of the flue gas produced by the coating reacting with fire. The water-based low smoke low toxicity thin type fire resisting coating for the steel structure comprises the following components: water soluble acrylic ester emulsion, low sulfur expandable graphite, ammonium polyphosphate, wollastonite, spherical closed poreexpanded perlite, a filler and an additive. The preparation method comprises the following steps: 1, mixing and grinding ammonium polyphosphate, wollastonite, the filler and water soluble acrylic ester emulsion; 2, adding water soluble acrylic ester emulsion, low sulfur expandable graphite, spherical closed pore expanded perlite and the additive, and agitating the raw materials evenly; and 3, adding water to adjust the viscosity of the coating. The invention is suitable for the coating carrying out the fire resisting protection on the steel structure and the preparation method thereof.
Description
technical field [0001] The invention relates to the technical field of coatings, in particular to a coating for fire protection of steel structures and a preparation method thereof. . Background technique [0002] Steel structures are widely used in modern buildings. However, the fire resistance of the steel structure is poor, and the mechanical strength of the steel decreases with the increase of the temperature. The bearing capacity of the commonly used construction steel decreases sharply at around 540°C. The general building fire fire scene temperature is mostly between 800 ~ 1200 ℃. The exposed steel structure will lose its bearing capacity and collapse in just over 10 minutes in the fire scene, causing heavy casualties and economic losses. Therefore, fire protection must be carried out on steel structures. Among various fire protection technical schemes, the use of steel structure fire retardant coatings to protect steel structures has the advantages of light weigh...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/08C09D5/18C09D7/12
Inventor 覃文清李风戚天游张泽江
Owner 应急管理部四川消防研究所