Manufacturing method of transparent pattern glass

Abstract

The invention relates to a manufacturing method of transparent pattern glass, comprising the following steps: 1. a wire mesh pattern printing plate is manufactured; 2. the glass is fed into a cleaning machine to be cleaned; 3. acid-proof ink is printed on the glass; 4. two pieces of glass are aligned, the four sides of the two pieces of glass are sealed with tapes, and then are frosted; 5. the frosted glass is put in a weak acid tank to be inflated and cleaned; 6. the glass is put in a gas polishing tank to be inflated and polished; 7. the ink on the polished glass is removed; 8. the glass is put in a cleaning bench to be cleaned with a water gun, and then the tapes on the four sides of the glass are removed; and 9. the glass is fed into a cleaning drier to be cleaned and dried, and then the finished product is manufactured. The method has the advantages that the adhered glass patterns are even and smooth, and have three-dimensional sense; anticorrosive material is not required to be coated on the back surface of the glass, the etching depths are uniform and smooth, the aesthetic feeling of the patterns is stronger, the quality is better, the requirements for producing high grade glass products can be greatly satisfied, the processing method is simple, the production cost can be greatly reduced, and the technology is environmental protection.

Description

technical field [0001] The invention relates to a production method of glass, in particular to a production method of light-transmitting three-dimensional pattern glass. Background technique [0002] At present, glass screen printing technology has matured, and various three-dimensional patterned glasses have appeared on the market, bringing convenience and fun to the use of home decoration and office space. The quality of the products is getting higher and higher, which is far from meeting people's needs for production or living techniques. As far as the current technology of producing light-transmitting three-dimensional pattern glass is concerned, due to the problems and defects of the manufacturing process, the produced light-transmitting pattern glass products are not satisfactory. The main problems are: the clarity of the glass pattern is poor, ink printing and baking The dry quality is not good, resulting in poor light transmittance, poor uniformity of ink pattern, p...

AI Technical Summary

Problems solved by technology

[0002] At present, glass screen printing technology has matured, and various three-dimensional patterned glasses have appeared on the market, bringing convenience and fun to the use of home decoration and office space. The quality is getting higher and higher, which is far from meeting people's needs for production or living technology.

As far as the current technology of producing light-transmitting three-dimensional pattern glass is concerned, due to the problems and defects of the manufacturing process, the produced light-transmitting pattern glass products are not satisfactory. The main problems are: the clarity of the glass pattern is poor, ink printing and baking The dry quality is not good, resulting in poor light transmittance, poor uniformity of ink pattern, polished glass lacks texture, and even affects the service life of glass quality, which brings inconvenience to consumers

Such as publication number: CN1181987C discloses a kind of production method of light-transmitting three-dimensional pattern glass, the pattern glass produced by its production method has poor light transmission, pattern definition is not good, and production efficiency is low, and cost is high, can not satisfy customer's requirement and need

The main technical defects that affect product quality are: 1. The problem of applying anti-corrosion materials on the back of the glass with printed patterns. The anti-corrosion materials themselves have certain corrosiveness to the glass. Lost the original translucent luster; 2. The problem of cleaning the glass anti-corrosion ink, which is difficult to clean, labor-intensive and time-consuming, and the effect is not good; 3. Air-drying after printing, drying affects the quality of the pattern; 4. The production process The cost of consumables; 5. The polishing process and the problem affecting product quality in the removal of polishing fluid; 6. The problem of production efficiency. In the production method of the prior art, only a single piece of glass can be produced in each process, such as smearing anti-corrosion Materials, corrosion with corrosive liquid, cleaning glass, etc., the process is complicated, not only the quality is poor, but also the efficiency is low

For this reason, the defects of the production process of the prior art lead to a single variety of glass products, poor artistic effects of glass patterns, and low grades of products, which cannot satisfy people's needs for high-quality, high-level material culture and spiritual and cultural life. need