SBS modified asphalt stabilizer and preparation method thereof
A modified asphalt and stabilizer technology, which is applied in building components, building insulation materials, buildings, etc., can solve the problems of easy segregation of asphalt, unstable storage, slow cross-linking speed, etc., and achieve uniform dispersion, fast cross-linking speed, avoid caking effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0017] Example 1:
[0018] Add 0.8 g of sulfur powder with a particle size of 100 mesh to 200 mesh into the high-speed disperser, and add 0.2 g of aromatic heterocyclic multifunctional olefin monomer. The heterocyclic multifunctional olefin monomer is divinylbenzene and trimethylolpropane. Trimethacrylate, diallyl phthalate, diol dimethacrylate or triallyl isocyanurate, stir for 30 minutes to make the two evenly mixed, then add to the grinder, grind for 30 minutes, Go through a 100-mesh sieve, then add the premix to 100g of rubber oil, aromatic oil or furfural oil at 100°C, start shearing for 15 minutes, and then obtain the SBS modified asphalt stabilizer product.
Example Embodiment
[0019] Example 2:
[0020] Add 0.7 grams of sulfur to the mixer, add 0.3 grams of divinylbenzene or trimethylolpropane trimethacrylate, stir for 15 minutes to make the two evenly mixed, then add to the grinder, grind for 15 minutes, and pass through a 100 mesh sieve , And then add the premix to 100g, 100℃ aromatic oil, start shearing for 15min, and then get SBS modified asphalt stabilizer product.
[0021] During the cross-linking process of the stabilizer of this embodiment, the cross-linking speed is blocky, the dispersion is uniform, and there is no block.
Example Embodiment
[0022] Example 3:
[0023] The SBS modified asphalt stabilizer of the present invention is prepared from the following raw materials in parts by weight ratio: 1 g of sulfur, 0.5 g of diallyl phthalate or divinylbenzene, and 99 g of rubber oil. The preparation method is the same as in Example 1.
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap