Method for preparing high-temperature resistant antibacterial non-stick paint

A non-stick coating, high temperature resistant technology, applied in anti-fouling/underwater coatings, coatings, paints containing biocides, etc., can solve the problem of easy breeding of bacteria, etc., and achieve obvious non-stick effect, obvious antibacterial effect, cost low cost effect

Inactive Publication Date: 2011-08-31
深圳佳德威油漆有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] But since most paints are based on organic compounds, bacteria can easily grow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high-temperature resistant antibacterial non-stick paint

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0014] Modified high temperature resistant silicone resin 65%

[0015] PTFE wax powder 5%

[0016] Talc 5%

[0017] Matting Powder 3.5%

[0018] Carbon black 1.5%

[0019] Propylene glycol methyl ether acetate 10%

[0020] Butanone 7%

[0021] Nano silver 0.2%

[0022] Dispersion aid 2%

[0023] Non-stick additive 0.8%

[0024] The manufacturing method of this embodiment is:

[0025] 1) First, put the modified high-temperature resistant silicone resin, polytetrafluoroethylene wax powder, talc powder, carbon black, nano-silver, propylene glycol methyl ether acetate, methyl ethyl ketone, and dispersing aid into a conventional dispersing machine for medium-speed dispersion 20-30 minutes;

[0026] 2) Mix and disperse, put talcum powder, carbon black, nano-silver, and matting powder into the original grinding machine for dispersing resin and additives, and make them grind and disperse at high speed together, and grind at high speed for 2-3 hours until the fineness less th...

specific Embodiment 2

[0030] Modified high temperature resistant silicone resin 65%

[0031] PTFE wax powder 5%

[0032] Talc 5%

[0033] Matting Powder 3.5%

[0034] Carbon black 1.5%

[0035] Propylene glycol methyl ether acetate 10%

[0036] Butanone 6.8%

[0037] Nanosilver 0.4%

[0038] Dispersion aid 2%

[0039] Non-stick additive 0.8%

[0040] The manufacturing method of this embodiment is:

[0041] 1) First, put the modified high-temperature resistant silicone resin, polytetrafluoroethylene wax powder, talc powder, carbon black, nano-silver, propylene glycol methyl ether acetate, methyl ethyl ketone, and dispersing aid into a conventional dispersing machine for medium-speed dispersion 20-30 minutes;

[0042] 2. Mix and disperse, put talcum powder, carbon black, nano-silver, and matting powder into the original grinding machine for dispersing resin and additives, and make them work together for high-speed grinding and dispersing, and high-speed grinding for 2-3 hours until the finen...

specific Embodiment 3

[0045] Modified high temperature resistant silicone resin 65%

[0046] PTFE wax powder 5%

[0047] Talc 5%

[0048] Matting Powder 3.5%

[0049] Carbon black 1.5%

[0050] Propylene glycol methyl ether acetate 10%

[0051] Butanone 6.6%

[0052] Nano silver 0.6%

[0053] Dispersion aid 2%

[0054] Non-stick additive 0.8%

[0055] The manufacturing method of this embodiment is:

[0056] 1) First, put the modified high-temperature resistant silicone resin, polytetrafluoroethylene wax powder, talc powder, carbon black, nano-silver, propylene glycol methyl ether acetate, methyl ethyl ketone, and dispersing aid into a conventional dispersing machine for medium-speed dispersion 20-30 minutes;

[0057] 2 Mix and disperse, put talcum powder, carbon black, nano-silver, and matting powder into the original grinding machine for dispersing resin and additives, and make them grind and disperse at high speed together, and grind at high speed for 2-3 hours until the fineness is less t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses high-temperature resistant antibacterial non-stick paint. The paint has remarkable antibacterial effect and obvious non-stick effect. A formulation of the paint basically comprises the following components: a, at least one resin accounting for 65 percent of the paint; b, wax powder accounting for 5 percent of the paint; and c, nano silver powder accounting for 0.2 to 0.6 percent of the paint. The formulation further comprises talc powder accounting for 5 percent of the paint, flatting powder accounting for 3.5 percent of the paint, butanone accounting for 6.6 to 7 percent of the paint, and carbon black accounting for 1.5 percent of the paint. The formulation further comprises dispersing aid accounting for 2 percent of the paint, and non-stick aid accounting for 0.8percent of the paint. The paint has the following advantages of good thermal stability, remarkable environmentally-friendly and antibacterial effects, obvious non-stick effect and preferable performance in the aspects of corrosion resistance, adhesive force, innocuousness, hardness and the like. Meanwhile, the paint has simple manufacturing process, low cost and better application prospect, and can well meet the demands of domestic markets.

Description

【Technical field】 [0001] The invention relates to a preparation method of a high-temperature-resistant antibacterial and non-stick coating applied to cooking utensils, medicine, food and special purposes, and belongs to the technical field of chemical coatings. 【Background technique】 [0002] Non-stick coating is a special coating whose coating surface is not easily adhered by other sticky substances or easily removed after adhesion. This kind of coating is widely used in household appliances, cooking utensils, automobiles, machinery, chemical industry and other industries due to its anti-adhesive properties such as extremely low surface energy, small friction coefficient and easy sliding. As a kind of environmentally friendly special coating with strong practicability and high technical content, non-stick coating has attracted more and more attention from coating research and development workers. The technology of non-stick coatings is complex, how to disperse fluororesin ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/04C09D5/14C09D5/00C09D7/12
Inventor 卢桂峰
Owner 深圳佳德威油漆有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap