Ceramic wine-bottle and preparation method thereof

A ceramic wine bottle and ceramic technology, which is applied in ceramic containers, ceramic molding machines, manufacturing tools, etc., can solve the problems of poor matching accuracy, low dimensional accuracy, and difficulty in anti-counterfeiting of metal bottle caps, and achieve reduced mold loss and high uniformity in size , angular effect

Active Publication Date: 2010-03-17
宜兴市昊源陶瓷厂(普通合伙)
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The accuracy of ceramic wine bottle mouth, especially the dimension accuracy of the outer mouth is low, resulting in poor matching accuracy with hard plastic and metal bottle caps with high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1: According to the required bottle mouth shape (such as full thread), the corresponding bottle mouth pressure injection steel mold is processed, and the prepared ceramic raw material (sintering temperature is higher than the bottle body 20℃) is processed into fine powder by dry ball milling, and the powder is added With 10wt% paraffin wax, the ceramic raw material fine powder and the paraffin wax are fully mixed in a mixer at about 80°C to obtain the hot-press grouting material. A semi-finished product molded bottle mouth molded body is obtained by a hot pressure grouting method. The semi-finished product is buried in fine alumina powder and the paraffin wax is burned out in a kiln at 800°C to obtain a semi-finished product without paraffin wax, which is then sintered in a kiln at 1190°C.

[0022] The sintered bottle mouth and the dry bottle body formed by grouting are bonded together with a glaze water binder (melting point temperature of 1100℃), and the sintered...

Example Embodiment

[0023] Example 2: Same as Example 1, in which the ceramic wine bottle is a sintered body after grouting, that is, the mouth and body are sintered, bonded and sintered again, the final size of the mouth and the design size deviation +0.08 mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melting temperatureaaaaaaaaaa
Login to view more

Abstract

The invention improves preparation method of ceramic wine-bottle and is characterized in that at least molding of the bottleneck is steel mold hot-press paraffin wax casting molding, after sintering the molded bottleneck, and cementing with a sintered or unsintered bottle body. The invention breaks through the technical problems that the precision of bottleneck of ceramic wine-bottle is low and the difficulty in solving bottleneck shaping limit; the requirement that ceramic wine-bottles have precise bottleneck dimension and diverse shaping variation like glass wine-bottles is realized; the uniformity of outer caliber dimension of the bottlenecks is high; the common difference of inner diameter and outer diameter can be less than or equal to 0.1mm; the yield, compared with the prior art, can be enhanced by at least 3%; the mold loss can be greatly reduced; the economic benefit is very obvious; the high requirements of wine market on sealing, opening, anti-counterfeiting of the wine-bottles can be completely satisfied; and matched use range of novel anti-counterfeiting bottle caps is widened, and irregular bottle caps such as full screw, fine screw and the like can be obtained, thusbeing applicable to ceramic wine-bottles, and initiating steel mold hot-press paraffin wax casting molding technique and sintering technique for at least the bottlenecks of ceramic wine-bottles.

Description

technical field [0001] The invention is an improvement to the preparation method of the ceramic wine bottle, and in particular relates to a preparation method of the ceramic wine bottle with high bottle mouth size precision and diversified outer bottle mouth shapes. Background technique [0002] Ceramic wine bottles have unique advantages, such as the function of aging and the diversity of appearance decoration. The dual-purpose function has gradually replaced the glass wine bottle, and has become the main container for dispensing wine. More and more attention has been paid to the packaging of wine, especially liquor. A large number of famous wines use ceramic wine bottles as containers. [0003] Ceramic wine bottle production, the prior art mainly adopts the grouting molding method, mainly contains three kinds: the first method: bottle body, bottleneck are formed by one-time grouting of same pair of moulds. However, due to the shrinkage rate from the semi-finished product ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/622B28B3/00B65D85/72B65D13/02
Inventor 吴骏
Owner 宜兴市昊源陶瓷厂(普通合伙)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products