Waterproof roll capable of carrying out chemical bonding and physical crosslinking synergism with concrete

A waterproof membrane and composite technology, which is applied in the direction of building construction, building insulation materials, textiles and papermaking, etc., can solve the problems that artificial methods cannot be peeled off, the operation is not easy to master, and the adhesive force is not durable, etc., to achieve reliable adhesion. knot effect, excellent tensile strength, low cost effect

Active Publication Date: 2011-07-06
XI NIU PI WATERPROOFING TECH CO LTD
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of manufacturing process makes the self-adhesive adhesive and the main material layer bond firmly, and it cannot be peeled off by artificial methods
[0005] The waterproof coiled material reported in the above-mentioned publication 1 has improved the bonding performance with wet concrete in some aspects, and it is also mentioned that the resin adhesive layer achieves waterproof effect due to the chemical reaction with concrete, but the use of high-density polyethylene membrane coiled material The strength is low when subjected to high temperature; the self-adhesive glue and polymer self-adhesive waterproof membrane composition reported in Document 2 have insufficient bonding force with the concrete base surface, the bonding force is not durable, and the operation is not easy to master

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof roll capable of carrying out chemical bonding and physical crosslinking synergism with concrete
  • Waterproof roll capable of carrying out chemical bonding and physical crosslinking synergism with concrete
  • Waterproof roll capable of carrying out chemical bonding and physical crosslinking synergism with concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] 3000 kilograms of matrix asphalt is placed in the reaction tank, and 200 kilograms of tackifier ordinary rubber powder, 200 kilograms of random polypropylene (APP) and 300 kilograms of styrene-butadiene-styrene block copolymer (SBS) are added, Mix evenly, then increase the temperature to 200-210°C, stir for 1.5-2h, then lower the temperature to about 180°C, then add 3000 kg filler bicarbonate powder, 100 kg plasticizer butyl naphthenate, 50 kg Antioxidant tris(2,4-di-tert-butylphenyl)phosphite and 60 kg of functional additive polymethylethoxysilane were added to the reaction tank, stirred for 0.5-1h, fully mixed and modified, and then transported to Colloid mill, the material is repeatedly ground, and then the modified asphalt compound is dip-coated on the polyester carcass, thickness control and setting, laminating, winding and other processes are prepared to prepare CPS wet paving / pre-paving with excellent performance waterproof materials.

Embodiment 2

[0050] Put 5000 kg of base asphalt in the reaction tank, add 150 kg of tackifier styrene-butadiene rubber and ordinary rubber powder, 300 kg of random polypropylene (APP) and 500 kg of styrene-butadiene-styrene block Copolymer (SBS), mix evenly, then raise the temperature to 200-210°C, stir for 1.5-2h, then lower the temperature to about 180°C, then add 2000 kg filler heavy calcium carbonate powder, 2000 kg talcum powder, 300 kg Plasticizer butyl naphthenate, 80 kilograms of antioxidant tris(2,4-di-tert-butylphenyl) phosphite, 80 kilograms of functional auxiliary agent polynaphthaldehyde sulfonic acid sodium salt are added to reaction tank, stir 0.5- 1h, fully mixed and modified, and then transported to the colloid mill, the material was repeatedly ground, and then the modified asphalt compound was dip-coated on the glass fiber matrix, thickness control and shaping, coating, winding and other processes were carried out. Prepare CPS wet-laid / pre-laid waterproof membrane with ex...

Embodiment 3

[0052] 2000 kilograms of matrix asphalt is placed in the reaction tank, and 100 kilograms of tackifier common rubber powder, 150 kilograms of random polypropylene (APP) and 200 kilograms of styrene-butadiene-styrene block copolymer (SBS) are added, Mix evenly, then increase the temperature to 200-210°C, stir for 1.5-2h, then lower the temperature to about 180°C, then add 1000 kg of filler bicarbonate powder, 1000 kg of asbestos powder, and 200 kg of plasticizer naphthenic acid Add butyl ester, 50 kg of antioxidant tris(2,4-di-tert-butylphenyl) phosphite, and 70 kg of functional additive polynaphthaldehyde sulfonic acid sodium salt into the reaction tank, stir for 0.5-1h, and fully mix and modify Then it is transported to the colloid mill, the material is repeatedly ground, and then the modified asphalt compound is dip-coated on the composite fiber matrix, the thickness is controlled and shaped, the film is coated, and the winding process is prepared into a CPS with excellent pe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a wet-laying and pre-laying waterproof roll which is made by the following processes: dipping and coating a modified asphalt compound on a blank body, controlling the thickness and sizing, coating a membrane, rolling, and the like, wherein the modified asphalt compound contains modified asphalt, a plasticizer, an antioxidant, a functional auxiliary agent and a filling gent. A preparation method of the waterproof roll comprises the following steps: putting substrate asphalt in a reaction pot, adding a thickening agent, irregular polyethylene and styrene-polybutadiene-styrene segmented copolymer, evenly mixing, heating and stirring for 1.5-2 hours, then reducing the temperature to about 180 DEG C, adding padding, the plasticizer, the antioxidant and the functional auxiliary agent into the reaction pot and stirring for 0.5-1h, evenly mixing and modifying, then conveying into a colloid mill for repeatedly milling to the material, then dipping and coating the modified asphalt on the blank body, controlling the thickness, sizing, coating the membrane and rolling, and finally preparing the waterproof roll which has excellent performance and can carry out chemical bonding and physical crosslinking synergism with the concrete, namely, a CPS waterproof roll for short.

Description

technical field [0001] The patent of the present invention relates to a waterproof coiled material, especially a wet-laid pre-paved waterproof coiled material capable of physically adsorbing mortise and tenon with concrete and at the same time chemically crosslinking and firmly bonded to concrete and its production method. Background technique [0002] Common waterproof materials mainly include coatings, coiled materials, sealants, and waterstops. The most used waterproof coatings are polyurethane, neoprene latex, and polymer cement waterproof coatings. They all have common problems in the use of coatings: such as construction The thickness is not easy to control; it is firmly combined with the base surface, and it is prone to "0" stretching and cracking due to cracks in the base surface; most coatings are not easy to use in long-term water immersion environments, and are not easy to use in places exposed to sunlight; especially polyurethane The waterproof coating used for c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04B1/66E04D5/02C08L95/00C08L53/02C08L9/06C08L23/12C08L21/00C08L83/06C08K13/02C08K5/526D06N5/00
Inventor 卢桂才伍盛江朱方伍郭文雄
Owner XI NIU PI WATERPROOFING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com