Red infrared-penetrating quartz tube and preparation method thereof

An infrared-transmitting, quartz tube technology, applied in glass manufacturing equipment, manufacturing tools, glass molding and other directions, can solve the problems of poor heating efficiency, high light transmittance, low refractive index, etc., to achieve wide light absorption range, filter light Stable performance and good uniformity

Active Publication Date: 2010-06-02
LIANYUNGANG HONGYANG QUARTZ PROD
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are two types of quartz glass tubes: transparent and milky white. Transparent quartz glass tubes have high light transmittance, low refractive ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] A red infrared-transmitting quartz tube, using SiO 2 The content is greater than 99.98%, the impurity content is less than 20ppm, and the high-purity quartz sand is 40-160 mesh. High-purity quartz sand is used as the basic raw material by weight, and 8% to 10% by weight of colorant is added.

[0021] Wherein the coloring agent is made up of the following raw materials of weight ratio:

[0022] Cuprous oxide Cu 2 O 0.1~0.5 Manganese dioxide MnO 2 1~3

[0023] Selenium Se 0.5~1 Cadmium sulfate octahydrate 3Cd 2 SO 4 ·8H 2 O 1~2

[0024] Aluminum hydroxide Al(OH) 3 0.5~1

[0025] SnCl dihydrate SnCl 2 2H 2 O 0.2~0.6

[0026] Samarium Chloride SmCl 3 1~2 antimony oxide Sb 2 o 3 1~2.

[0027] The optimum weight portion of the coloring agent is 9%-9.5% of the high-purity quartz sand.

[0028] The formula one of coloring agent:

[0029] Cuprous oxide Cu 2 O 0.5 Manganese dioxide MnO 2 3

[0030] Selenium Se 1 Cadmium Sulfate Octahydrate 3Cd 2 SO...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a red infrared-penetrating quartz tube. Highly-pure arenaceous quartz is used as a basic material in part by weight, and 8-10% of colorant by weight is added, wherein the colorant comprises cuprous oxide (Cu2O), manganese dioxide (MnO2), selenium (Se), cadmium sulfate octahydrate (3Cd2SO4.8H2O), aluminium hydroxide (Al(OH)3), stannous chloride dehydrate (SnCl2.2H2O), samarium chloride (SmCl3) and antimony oxide (Sb2O3). The red infrared-penetrating quartz tube which is formed by drawing by adopting a preparation technique for tube wall integral coloring has favorable uniformity and toughness, strong compression resistance and wide light-absorbing range, has the characteristics of high temperature resistance and stable filtering property, and absorbs visible light and penetrates the near infrared ray of 800-2500nm. The invention has the spectral characteristics of 400nm penetration rate T being less than or equal to 14%, 700nm penetration rate T being less than or equal to 6.0% and 1100nm penetration rate T being more than or equal to 85.0% when the thickness of a sample is 1.0 mm.

Description

technical field [0001] The invention relates to a preparation technology of a quartz tube, in particular to a red infrared-transmitting quartz tube. The invention also relates to a preparation method of the quartz tube. Background technique [0002] The thermal expansion coefficient of quartz glass is small, and it has the characteristics of high temperature resistance, ultraviolet and infrared transmission, and has been more and more widely used in industrial and civilian products. At present, there are two types of quartz glass tubes: transparent and milky white. Transparent quartz glass tubes have high light transmittance, low refractive index, and poor heating efficiency; milky white quartz glass tubes use air bubbles as the dispersed phase, although they heat up quickly. , but its uniformity is poor. Contents of the invention [0003] The technical problem to be solved by the present invention is to address the deficiencies of the prior art, and propose a red infrar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C4/10C03C3/06C03B20/00
Inventor 徐传龙
Owner LIANYUNGANG HONGYANG QUARTZ PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap