Magnesite micro powder-assisting flame-resistant expanded halogen-free flame-resistant electronic wire-coated material and preparation method thereof

A technology of auxiliary flame retardant and auxiliary flame retardant, applied in the field of wire material, can solve the problems of low physical properties, high price, poor water resistance, etc., and achieve the effect of excellent physical properties and low price

Inactive Publication Date: 2010-06-02
NINGBO SHIP PLASTIC CO LTD
View PDF1 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The problem to be solved by the present invention is that the flame retardant effect of the current halogen-free electronic wire outer covering is not ideal, the physical propertie

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnesite micro powder-assisting flame-resistant expanded halogen-free flame-resistant electronic wire-coated material and preparation method thereof
  • Magnesite micro powder-assisting flame-resistant expanded halogen-free flame-resistant electronic wire-coated material and preparation method thereof
  • Magnesite micro powder-assisting flame-resistant expanded halogen-free flame-resistant electronic wire-coated material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] Magnesite micropowder auxiliary flame retardant expanded halogen-free flame retardant electronic wire outer quilt contains basic resin, compatibilizer, flame retardant, auxiliary flame retardant, lubricant, antioxidant; the basic resin is high-density poly One or more mixtures of ethylene, low density linear polyethylene, metallocene polyethylene, POE, EVA; the compatibilizer is one or more mixtures of PE-g-MAH and mPE-g-MAH ; The anti-drip agent is polytetrafluoroethylene, the antioxidant is at least one of hindered phenols, phosphites, and hindered amine antioxidants, and the flame retardant A is a phenolic resin The microcapsules of the capsule wall are coated with ammonium polyphosphate, the flame retardant B is melamine, and the flame retardant C is one or more mixtures of pentaerythritol, dipentaerythritol, and tripentaerythritol; the auxiliary flame retardant The agent is a modified micron-level magnesite powder, and the fractions of the described raw materials a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a magnesite micro powder-assisting flame-resistant expanded halogen-free flame-resistant electronic wire-coated material and a preparation method thereof. The material consists of 100 parts of basic resin, 5-25 parts of compatilizer, 20-40 parts of fire retardant A, 10-30 parts of fire retardant B, 0-10 parts of fire retardant C, 5-25 parts of assistant fire retardant, 0-0.1 part of anti-dripping agent, 0.1-2 parts of lubricating agent and 0.1-1 part of antioxygen, wherein the fire retardant A is microcapsule-coated ammonium polyphosphate, the microcapsule takes phenolic resin as capsule wall, and the assistant fire retardant is modified micrometer-level magnesite micro powder. The material has good physical performance, does not obtain poisonous and harmful substances, does not release poisonous gas when burning, has good flame resistance, higher extension-resistant and breaking elongation ratio than congeneric products, higher flame-resistant effect than the congeneric halogen-free flame-resistant electric wire and cable material, greatly reduce the price, and particularly can be fast popularized in an industrialization way and applied in a marketization way due to the low price as high-grade magnesite resource is abundance in China.

Description

technical field [0001] The invention relates to a wire material with polyolefin as the main base material, in particular to a halogen-free expanded flame-retardant electronic wire outer quilt with magnesite micropowder as an auxiliary flame-retardant and a preparation method thereof. Background technique [0002] At present, the commonly used high flame retardant wire and cable materials are mainly made of PVC materials. Although it has high flame retardant efficiency and good temperature resistance, due to the plasticizers that must be used in the production of PVC wire and cable materials, it will be more or less affected. Influence on the human body. Wires and cables containing a large amount of halogens will release toxic and harmful gases in the event of fire and combustion, which is the main cause of casualties in closed spaces such as high-rise buildings or dance halls. PVC wire and cable materials are used in insulating layers. The electrical properties such as volum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08L23/08C08L23/00C08L31/04C08K13/06C08K9/10C08K3/32C08K5/3492C08K5/053C08K9/04C08K9/06C08K3/26C09C1/00C09C3/10C09C1/02C09C3/12C09C3/08H01B7/295H01B3/44
Inventor 刘华罗英勇戴利萍张文阳
Owner NINGBO SHIP PLASTIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap