A preparation method of polyolefin microporous membrane with symmetrical upper and lower surface structures

A polyolefin microporous film and surface structure technology, applied in flat products, household components, applications, etc., can solve the problems of poor air permeability, asymmetrical size of micropores, asymmetric heating, etc. The effect of symmetrical and uniform pore structure

Active Publication Date: 2012-02-15
SHENZHEN SENIOR TECH MATERIAL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this way, the casting method causes the upper and lower surfaces of the thick sheet to be heated asymmetrically. During the cooling-induced phase separation process, the phase separation degree is different, and the size of the micropores formed after the subsequent extraction is asymmetrical. The structure of the microporous membrane is uneven and the air permeability is not good.
Moreover, due to the asymmetric shrinkage of the upper and lower surfaces, the microporous membrane is warped and deformed.
When the prepared microporous membrane is used as a lithium-ion battery separator, it has poor air permeability, low lithium ion penetration ability, and poor battery performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of polyolefin microporous membrane with symmetrical upper and lower surface structures

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] 10% (weight) of high-density polyethylene (melting point 133° C.) is dropped into a twin-screw extruder (78 mm in diameter, L / D=50, strong mixing type), and 90 % (weight) of liquid paraffin (kinematic viscosity 90cst / 40°C), melted and kneaded under the conditions of 200°C and 150 rpm to form a solution, and passed the solution through a T-type die (die lip opening 0.8mm , die head temperature 180 ℃) and two rollers with symmetrical diameters to obtain thick sheets after casting, the diameter of the rollers is 200 mm, and the temperature of the rollers is 15 ℃. On the basis of preheating the thick sheet, it is stretched by biaxial stretching equipment, the preheating time is 10S, the preheating temperature is 100°C, and the stretching ratio is 3×3 times (that is, the longitudinal stretching ratio is 3 times, and the transverse stretching ratio is 3 times); Then do the setting treatment, the treatment temperature is 100°C, and the treatment time is 10s; finally, the liqui...

Embodiment 2

[0029]60% (weight) of polypropylene (melting point 167° C.) is dropped into a twin-screw extruder (78 mm in diameter, L / D=50, strong mixing type), and 40% ( weight) of liquid paraffin (kinematic viscosity 90cst / 40°C), melted and kneaded at 200°C and 150 rpm to prepare a solution, and passed the solution through a T-shaped die (die lip opening 0.8mm, die Head temperature 240 ℃) and two diametrically symmetrical rollers to obtain a slab, the diameter of the roller is 1000mm, and the roller temperature is 50 ℃. On the basis of preheating the thick sheet, it is stretched by biaxial stretching equipment, the preheating temperature is 150°C, and the stretching ratio is 5×9 times (that is, the longitudinal stretching ratio is 5 times, and the transverse stretching ratio is 9 times); The treatment temperature is 150°C, and the treatment time is 100s; finally, the liquid paraffin in the film is extracted with methyl ethyl ketone, and after drying, it is subjected to transverse stretchi...

Embodiment 3

[0031] Put 20% (weight) polyethylene (melting point 133°C) into the internal mixer with a preset temperature of 180°C, and add 80% (weight) dioctyl phthalate through the side feeding port with a metering pump Esters were melted and kneaded at 200°C and 150 rpm to prepare a solution, and the solution was cast through a hanger-type die (the opening of the die lip was 0.8mm, and the temperature of the die head was 200°C) and two rollers with symmetrical diameters. Thick sheets were obtained after sheeting, the diameter of the roller was 800mm, and the temperature of the roller was 15°C. The thick sheet is preheated on the basis of biaxial stretching, the preheating temperature is 125°C, and the stretching ratio is 3×3 times (that is, the longitudinal stretching ratio is 3 times, and the transverse stretching ratio is 3 times); then the setting treatment is performed, and the processing temperature is 125°C , the processing time is 10s; finally, the dioctyl phthalate in the film i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a method for preparing a polyolefin microporous membrane with a symmetrical upper and lower surface structure, comprising the following steps: 1) mixing a polyolefin resin with a diluent, and the weight ratio of the polyolefin resin to the diluent is 1-6: 4-9; 2) Extruding the above mixture through a die through a die to obtain a thick sheet after being extruded by a cold roll casting method; 3) Preheating the thick sheet and then stretching it vertically and horizontally; 4) Shaping treatment; 5) Extracting the diluent and drying; 6) Transverse stretching and setting treatment; 7) Winding. For the polyolefin microporous membrane prepared by the above process steps, especially a set of rollers with the same diameter are installed on the upper and lower surfaces of the thick sheet, or on the conventional cold roller and air knife auxiliary placement device, a set of rollers is installed on one side of the air knife. Thick sheets are obtained by cooling with the aid of roller sets, and then stretched and extracted for the thick sheets, finally a product with symmetrical and uniform microporous structure on the upper and lower surfaces and good air permeability can be obtained, without warping and deformation.

Description

technical field [0001] The invention relates to a preparation method of a polyolefin microporous membrane, in particular to a preparation method of a polyolefin microporous membrane with symmetrical upper and lower surface structures. Background technique [0002] Polyolefin microporous film is a plastic film with numerous interconnecting micropores with a pore size in the range of 0.01-10 μm. It has been widely used in separators for lithium-ion batteries. The industrial production methods of this kind of microporous membrane at home and abroad mainly include melt stretching method and thermally induced phase separation method. [0003] The melt stretching method (that is, the dry method) is to extrude a crystalline polymer (such as polypropylene) into a film under the condition of increasing the stress of the molten polymer, and then anneal the film under no tension or low tension to obtain the necessary crystallization. structure, and then longitudinally stretched to pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C55/12C08J9/00C08J9/26C08J9/28C08L23/00C08L23/12C08L23/08C08L23/20C08K13/02B29C47/14B29C47/88B29C48/08B29C48/305
CPCC08L2203/16C08J2323/02B29C47/0057B29C47/8805B29C47/0042B29L2007/002C08L23/04B29C47/0019B29C47/0021B29C55/12B29C55/08B29K2023/00B29C55/18B29L2031/755C08J5/18B29K2105/04C08L23/02B29C47/14B29C48/07B29C48/08B29C48/0012B29C48/0018B29C48/305B29C48/91B29C48/914B29C48/917C08L2666/06
Inventor 陈秀峰高东波陈勇
Owner SHENZHEN SENIOR TECH MATERIAL