Aluminum-silicon-zinc-rare earth-magnesium-ferrum-copper-chromium-containing hot dip coating alloy and method for preparing same

A hot-dip plating and alloying technology, which is applied in hot-dip plating process, metal material coating process, coating, etc., can solve the problems of contact corrosion, loss of anti-corrosion effect, wear and other problems, and achieve the improvement of contact corrosion resistance. Contact corrosion problems, the effect of expanding applications

Active Publication Date: 2010-06-16
JIANGSU LINLONG NEW MATERIALS CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, although some achievements have been made in the prevention of contact corrosion of titanium alloys at home and abroad, there are certain problems in the current methods, mainly because the coating layer used is easy to lose the protective effect under the synergistic effect of environment and stress. Conventional methods on the surface of titanium alloys The plating coating is easy to peel off under the contact load, and it is easy to lose the anti-corrosion effect. The peeled off fragments cause abrasive wear between the contact parts and aggravate the failure of the parts. Therefore, a large number of titanium alloy fasteners in the aircraft are urgently needed. Need to address failures due to contact corrosion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum-silicon-zinc-rare earth-magnesium-ferrum-copper-chromium-containing hot dip coating alloy and method for preparing same
  • Aluminum-silicon-zinc-rare earth-magnesium-ferrum-copper-chromium-containing hot dip coating alloy and method for preparing same
  • Aluminum-silicon-zinc-rare earth-magnesium-ferrum-copper-chromium-containing hot dip coating alloy and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The hot-dip alloy is made of aluminum, silicon, zinc, magnesium, iron, copper, chromium, rare earth elements and TiO 2 Composed of nano-oxide particle reinforcement, the percentages of each component to the total mass are: silicon content: 8-24%, zinc content: 1.2-3.1%, rare earth element content: 0.02-0.5%, magnesium content: 0.5-3.2% %, iron content: 0.05-1%, copper content: 0.05-0.5%, chromium content: 0.5-2.0%, TiO 2 Content: 1 to 2%, the balance is aluminum, see the following table 1 for details:

[0043] Table 1: The mass percentage content (%) and related index parameters of each component in the total weight

[0044]

Embodiment 2

[0046] The hot-dip alloy is made of aluminum, silicon, zinc, magnesium, iron, copper, chromium, rare earth elements and CeO 2 Composed of nano-oxide particle reinforcement, the percentages of each component to the total mass are: silicon content: 8-24%, zinc content: 1.2-3.1%, rare earth element content: 0.02-0.5%, magnesium content: 0.5-3.2% %, iron content: 0.05~1%, copper content 0.05~0.5%, chromium content: 0.5~2.0%, CeO 2 Content: 1 to 2%, the balance is aluminum, see the following table 2 for details:

[0047] Table 2: The mass percentage content (%) and related index parameters of each component in the total weight

[0048]

Embodiment 3

[0050] The hot-dip alloy is composed of aluminum, silicon, zinc, magnesium, iron, copper, chromium, rare earth elements and nano-oxide particle reinforcement, wherein the nano-oxide particle is TiO 2 and CeO 2 , and TiO 2 and CeO 2 The ratio is 1: (1-3), and the percentages of each component to the total mass are: silicon content: 8-24%, zinc content: 1.2-3.1%, rare earth element content: 0.02-0.5%, magnesium content: 0.5% ~3.2%, iron content: 0.05~1%, copper content 0.05~0.5%, chromium content: 0.5~2.0%, TiO 2 and CeO 2 The total content of aluminum alloy: 1~2%, the balance is aluminum, see the following table 3 for details:

[0051] Table 3: The mass percentage content (%) and related index parameters of each component accounting for the total weight

[0052]

[0053] In embodiment 1-3, preferably, wherein each component accounts for the total mass percentage as follows: silicon content: 12-20%, zinc content: 1.5-2.5%, rare earth element content: 0.1-0.3%, magnesium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to hot dip coating alloy specially used for surface coatings of titanium alloy parts. The hot dip coating alloy consists of aluminum, silicon, zinc, rare earth elements, magnesium, ferrum, copper, chromium and reinforcing agent of particles of nano oxides, and based on the total weight of the alloy, the alloy comprises 8 to 24 percent of silicon, 1.2 to 3.1 percent of zinc, 0.02 to 0.5 percent of rare earth elements, 0.5 to 3.2 percent of magnesium, 0.05 to 1 percent of ferrum, 0.05 to 0.5 percent of copper, 0.5 to 2.0 percent of chromium, 1 to 2 percent of reinforcing agent of particles of nano oxides, and the balance of aluminum and inevitable impurities, wherein the reinforcing agent of the particles of the nano oxides may be one or two of TiO2 and CeO2. The hot dip coating alloy produced by the method can form a coating with good corrosion resistance and wearing resistance and good metallurgical bonding property with a matrix on the surface of the titanium alloy.

Description

technical field [0001] The invention relates to a hot-dipping alloy containing aluminum-silicon-zinc-rare earth-magnesium-iron-copper-chromium for surface coating of titanium alloy parts and a preparation method thereof. Background technique [0002] Titanium alloy has the advantages of high strength and strong corrosion resistance, so it has become an important aerospace material. The use of titanium alloy is of great significance to reduce the weight of the aircraft and improve the performance of the aircraft. However, titanium alloy itself has good corrosion resistance. However, when it is in contact with aluminum alloy and alloy steel, under the synergistic effect of stress and environment, it is prone to contact corrosion and lead to failure. [0003] Contact corrosion is a kind of galvanic corrosion, that is, dissimilar metals are in contact in the same medium. Due to the different metal potentials, the metal with a lower potential dissolves faster, resulting in loca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C2/12C22C21/02C22C1/02
Inventor 冯立新张敏燕张平则
Owner JIANGSU LINLONG NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com