Production method of high wet modulus bamboo pulp viscose glue fiber

A technology of viscose fiber and production method, which is applied in the field of viscose fiber production, can solve the problems of inconvenient continuous dyeing process, poor mercerizing ability, low wet modulus, etc., and achieve excellent dyeability, bright color and high alkalinity The effect of stability

Active Publication Date: 2010-06-16
刘泳
View PDF1 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the fabric is easily deformed by rubbing force during washing, and it is easy to shrink after drying, and its size is unstable.
Therefore, the blended fabric of bamboo cellulose fiber and cotton prepared by this process is relatively poor in the mercerizing treatment ability to improve the appearance of the fabric
Another disadvantage is that the fabric must be dyed in a loose type, because the wet modulus is not high. If the dyeing process is carried out under tension, the fabric will shrink violently during use. Therefore, it is inconvenient for the dyeing process to be carried out continuously.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] a. Impregnation: immerse the cellulose bamboo pulp in an immersion tank filled with caustic soda solution. Denaturant composition, the addition amount is 0.2% of methylcellulose, wherein in the denaturant composition: highly yellowed castor oil 20%, V-388 denaturant 45%, Lv-3 denaturant 35%;

[0025] b. Squeeze and pulverize: squeeze the impregnated raw materials with a squeeze machine, and then pulverize them with a pulverizer, wherein the squeeze ratio is 2.0, and the pulverization degree is 180g / L;

[0026] c. Aging: put the pulverized raw materials into the aging drum for aging operation, adopt the low temperature method, control the aging temperature at 25°C, and the aging time is 45 minutes;

[0027] d. Yellowing: Add the aged raw materials into the yellowing machine to react with carbon disulfide. The technical parameters are: the amount of carbon disulfide added is 50% of that of methyl cellulose, the yellowing time is 50 minutes, the temperature is 30°C, and th...

Embodiment 2

[0034] a. Impregnation: immerse the cellulose bamboo pulp in an immersion tank filled with caustic soda solution. Denaturant composition, the addition amount is 0.4% of methylcellulose, wherein in the denaturant composition: highly yellowed castor oil 50%, V-388 denaturant 20%, Lv-3 denaturant 30%;

[0035] b. Squeeze and pulverize: squeeze the impregnated raw materials with a squeeze machine, and then pulverize them with a pulverizer, wherein the squeezing multiple is 2.4, and the pulverization degree is 150g / L;

[0036] c. Aging: put the pulverized raw materials into the aging drum for aging operation, adopt the low temperature method, control the aging temperature at 20°C, and the aging time is 120 minutes;

[0037] d. Yellowing: Add the aged raw materials into the yellowing machine to react with carbon disulfide. The technical parameters are: the amount of carbon disulfide added is 60% of that of methyl cellulose, the yellowing time is 100 minutes, the temperature is 20°C,...

Embodiment 3

[0044] a. Impregnation: Immerse the cellulose bamboo pulp in an impregnation barrel filled with caustic soda solution. Denaturant composition, the addition amount is 0.3% of methyl cellulose, wherein in the denaturant composition: highly yellowed castor oil 45%, V-388 denaturant 40%, Lv-3 denaturant 15%;

[0045] b. Squeeze and pulverize: squeeze the impregnated raw materials with a squeeze machine, and then pulverize them with a pulverizer, wherein the squeeze ratio is 2.2, and the pulverization degree is 165g / L;

[0046] c. Aging: Put the pulverized raw materials into the aging drum for aging operation, adopt low temperature method, control the aging temperature at 22°C, and the aging time is 80 minutes;

[0047] d. Yellowing: Add the aged raw materials into the yellowing machine to react with carbon disulfide. The technical parameters are that the amount of carbon disulfide added is 55% of that of methyl cellulose, the yellowing time is 70 minutes, and the temperature is 25...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pulverizationaaaaaaaaaa
pulverizationaaaaaaaaaa
pulverizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method of high wet modulus bamboo pulp viscose glue fiber, which adopts the steps of dipping, squeezing, smashing, maturing, yellowing, spinning, drawing, refining, drying and the like to prepare high wet modulus bamboo pulp viscose glue fiber. The high wet modulus bamboo pulp viscose glue fiber prepared with the method of the invention has dry breaking strength of 3.2-3.8 CN / dtex, wet breaking strength of 2.0-2.4 CN / dtex and wet modulus of 0.60-0.65 CN / dtex, has the characteristics of high humidity modulus, better purity, favourable affinity for dyestuff, non-fibrillation, non-fibrillar structure and the like, reduces expansion, reduces water retention capacity and improves alkali stability. Prepared fabric has silky luster and draping property, is extremely soft, has excellent dyeability and vivid luster and can keep bright and colorful after being cleaned several times.

Description

technical field [0001] The invention relates to a production method of viscose fiber, in particular to a production method of high wet modulus bamboo pulp viscose fiber. Background technique [0002] In the textile spinning industry, according to the processing method of bamboo fiber, bamboo fiber can be divided into two types: primary bamboo fiber and regenerated bamboo fiber. Raw bamboo fiber is bamboo fiber made by physical method, and regenerated bamboo fiber is bamboo pulp fiber made by chemical method. [0003] Raw bamboo fiber is made by rolling, twisting and combing bamboo by physical and mechanical methods, and then degumming bamboo fiber, removing sugar, fat, disinfecting and drying. Bamboo fiber has the advantages of coolness, moisture absorption, breathability, and perspiration, and has natural antibacterial properties, which has attracted the attention of the international market. However, due to its natural nature and long processing steps, the fineness and o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01C1/00D01D1/02D01D5/06D01F2/06
Inventor 吴会俊熊桐生赵睿哲
Owner 刘泳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com