Transparent ABS material and preparation method thereof

An ABS material and transparent technology, applied in the field of transparent ABS materials and its preparation, can solve the problems of easy accumulation of large static charges, affecting the appearance of products, catastrophic accidents, etc., achieve excellent transparency, broad application prospects, and good chemical resistance Effect

Inactive Publication Date: 2010-08-18
SHENZHEN KEJU NEW MATERIAL
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the molecular structure of ABS determines that it is a poor conductor, and it is easy to accumulate a large amount of static charge during use.
The electrostatic attraction is easy to absorb dust and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] Example one:

[0024] Dry the ABS raw materials at 80°C for 3 hours, and weigh the raw materials according to the following weight percentages: ABS 90%, main antistatic agent 5%, auxiliary antistatic agent 3%, and high temperature antioxidant 2%;

[0025] First, premix the main antistatic agent, auxiliary antistatic agent and high temperature antioxidant for 2-3 minutes, then add the dried ABS and premixed materials to the high-speed batching mixer, and mix for 5 to 8 minutes;

[0026] Put the mixed material in a single-screw machine for melt extrusion and granulation. The process is as follows: single screw first stage temperature 170-280°C, second stage temperature 180-190°C, third stage temperature 190-200°C, mold temperature 30-60°C, residence time 1-2 minutes, pressure 10-15MPa.

Example Embodiment

[0027] Embodiment two:

[0028] Dry the ABS raw materials at 80°C for 3 hours, and weigh the raw materials according to the following weight percentages: ABS 93%, main antistatic agent 5%, auxiliary antistatic agent 1%, high temperature antioxidant 1%;

[0029] First, premix the main antistatic agent, auxiliary antistatic agent and high temperature antioxidant for 2-3 minutes, then add the dried ABS and premixed materials to the high-speed batching mixer, and mix for 5 to 8 minutes;

[0030] Put the mixed material in a single-screw machine for melt extrusion and granulation. The process is as follows: single screw first stage temperature 170-280°C, second stage temperature 180-190°C, third stage temperature 190-200°C, mold temperature 30-60°C, residence time 1-2 minutes, pressure 10-15MPa.

Example Embodiment

[0031] Example three:

[0032] Dry the ABS raw materials at 80°C for 3 hours, and weigh the raw materials according to the following weight percentages: ABS 95%, main antistatic agent 2%, auxiliary antistatic agent 2%, high temperature antioxidant 1%;

[0033] First, premix the main antistatic agent, auxiliary antistatic agent and high temperature antioxidant for 2-3 minutes, then add the dried ABS and the premixed materials to the high-speed batching mixer, and mix for 5 to 8 minutes;

[0034] Put the mixed materials in a single-screw machine for melt extrusion and granulation. The process is as follows: single screw first stage temperature 170-280°C, second stage temperature 180-190°C, third stage temperature 190-200°C, mold temperature 30-60°C, residence time 1-2 minutes, pressure 10-15MPa.

[0035] The performance test and characterization are based on the relevant ASTM standards; the test conditions are 23°C and 53% relative humidity.

[0036] Tensile strength / elongation at break:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a transparent ABS material and a preparation method thereof. The transparent ABS material comprises the following components by weight percentage: 90-95 percent of ABS, 2-5 percent of main anti-static agent, 1-3 percent of auxiliary anti-static agent and 1-2 percent of high-temperature antioxidant. The transparent ABS material maintains the advantages of the ABS such as easy processing and formation, excellent corrosion resistance, excellent chemical resistance and the like, and also has the advantages of excellent transparency, excellent anti-static effect and permanent anti-static properties. Therefore, the transparent ABS material can substitute glass in various fields, and has broad application prospects in such industries as electrical appliances, instruments,automobiles, medical appliances and electronics.

Description

[technical field] [0001] The invention relates to the technical field of polymer materials, in particular to a transparent ABS material and a preparation method thereof. [Background technique] [0002] Acrylonitrile-butadiene-styrene copolymer (Acrylonitrile ButadieneStyrene, ABS) is currently the largest and most widely used polymer. It organically unifies the various properties of PS, SAN, and BS, and has excellent mechanical properties of toughness, hardness, and rigid phase balance. It has excellent impact strength, good dimensional stability, electrical properties, wear resistance, chemical resistance, dyeability, good molding and machining. However, the molecular structure of ABS determines that it is a poor conductor, and it is easy to accumulate a large amount of static electricity during use. The electrostatic attraction is easy to absorb dust and some dirt in the air, which affects the appearance of the product; especially when the static electricity accumulates ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L55/02C08L71/00C08K5/42C08K5/526B29B9/06B29C47/92B29C48/92
CPCB29C48/9185B29C48/04B29C48/397B29C48/92B29C2948/92514B29C2948/92561B29C2948/92704B29C2948/92895B29C2948/92904
Inventor 徐东徐永何杰
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap